KetaSpire® KT-880 GF20

Category:	PEEK , Polyetheretherketone
Manufacturer:	Solvay Specialty Polymers
Trademark:	KetaSpire®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	INPh32_KetaSpire-KT-880-GF20.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

KetaSpire® KT-880 GF20 is a high flow, 20% glass-fiber reinforced grade of polyetheretherketone (PEEK). This resin offers higher strength and stiffness properties relative to unreinforced KetaSpire® PEEK resin. The glass fiber content is optimized to provide a balance of strength and stiffness with toughness-related properties, such as impact resistance and elongation at break. This level of reinforcement also affords greater mechanical robustness in structural applications, particularly those with service temperatures approaching 300°C (572°F).

KetaSpire® PEEK is produced to the highest industry standards and is characterized by a distinct combination of properties, which include excellent wear resistance, best-in-class fatigue resistance, ease of melt processing, high purity and excellent chemical resistance to organics, acids and bases.

These properties make it well-suited for applications in healthcare, transportation, electronics, chemical processing and other industrial uses.

General Information
Filler / Reinforcement	Glass Fiber, 20% Filler by Weight
Features	Autoclave Sterilizable Biocompatible E-beam Sterilizable Ethylene Oxide Sterilizable Fatigue Resistant Flame Retardant Good Chemical Resistance Good Dimensional Stability Good Sterilizability Heat Sterilizable High Flow High Heat Resistance High Stiffness High Strength Radiation (Gamma) Resistant Radiation Sterilizable Radiotranslucent Steam Resistant Steam Sterilizable
Uses	Aircraft Applications Automotive Applications Connectors Dental Applications Electrical/Electronic Applications Film Hospital Goods Industrial Applications Medical Devices Medical/Healthcare Applications Oil/Gas Applications Pump Parts Seals Surgical Instruments
RoHS Compliance	Contact Manufacturer
Appearance	Tan
Forms	Pellets
Processing Method	Injection Molding

Physical	Nominal Value	Unit	Test Method
Density	1.46	g/cm³	ISO 1183
Water Absorption (24 hr)	0.022	%	ISO 15512
Ash Content	20	%	ISO 3451-1

Mechanical	Nominal Value	Unit	Test Method
Modulus of Elasticity	8.24	GPa	ISO 527
Tensile Stress (Break)	162	MPa	ISO 527-2
Tensile Strain (Break)	3.5	%	ISO 527-2/1A/5
Flexural Modulus	7720	MPa	ISO 178
Flexural Stress	238	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength	60	kJ/m²	ISO 179
Notched Izod Impact Strength	6.0	kJ/m²	ISO 180

Thermal	Nominal Value	Unit	Test Method
Melting Temperature ¹	345	°C	ISO 11357

Injection	Nominal Value	Unit
Drying Temperature	150	°C
Drying Time	4.0	hr
Rear Temperature	365	°C
Middle Temperature	371	°C
Front Temperature	377	°C
Nozzle Temperature	382	°C
Mold Temperature	177 to 204	°C
Injection Rate	Fast
Screw Compression Ratio	2.5:1.0 to 3.5:1.0

Note Message
1 .	DSC First heat

Resin Grade	Manufacturer	Category	Trademark
SABIC® LLDPE 6821W	Saudi Basic Industries Corporation (SABIC)	LLDPE	SABIC® LLDPE
Stat-Tech™ ATC-000/000 AS Natural	PolyOne Corporation	Acetal (POM) Copolymer	Stat-Tech™
Braskem EVA 3019 PE	Braskem	EVA	Braskem EVA
Fainplast PVC RE 410	Fainplast Compounds S.r.l	PVC, Rigid	Fainplast PVC
OTECH TPE OTO7510 - Profile	OTECH Corporation	TPE	OTECH TPE