SABIC® LDPE 2501N0W
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | INE8RU_SABIC-LDPE-2501N0W.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® LDPE 2501N0W is a grade without additives with a low gel level, which combines good draw down ability with fair optical properties and stiffness. Application SABIC® LDPE 2501N0W is typically used in diaper film, surface protection film, lamination film and in applications where low blocking behaviour is required and the presence of slip and anti block is unwanted. SABIC® LDPE 2501N0W can typically be used for food applications due to very low migration levels. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.925 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.75 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (Blown Film) | 0.90 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Elastic Modulus - MD (50 µm, Blown Film) | 200 | MPa | ASTM D882 |
| Elastic Modulus - TD (50 µm, Blown Film) | 200 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 50 µm, blown film | 12.0 | MPa | ASTM D882 |
| TD : Yield, 50 µm, blown film | 12.0 | MPa | ASTM D882 |
| MD : Broken, 50 µm, blown film | 25.0 | MPa | ASTM D882 |
| TD : Broken, 50 µm, blown film | 20.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 50 µm, blown film | > 200 | % | ASTM D882 |
| TD : Broken, 50 µm, blown film | > 500 | % | ASTM D882 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Impact Strength - Blown FIlm (50.0 µm) | 150 | J/cm | ASTM D4272 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Blocking - Blown Film (50.0 µm) | 20 | g | Internal method |
| Re-blocking - Blown Film (50.0 µm) | g | Internal method | |
| Tear Strength 1 | ISO 6383-2 | ||
| MD : 50.0 µm | 45.0 | kN/m | ISO 6383-2 |
| TD : 50.0 µm | 45.0 | kN/m | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 98.0 | °C | ISO 306/A |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (50.0 µm, Blown Film) | 10 | % | ASTM D1003A |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film properties have been measured at film of 50 µm with a BUR of 3.The film has been produced on Kiefel IBC blown film line with 200 kg/h. Die size 200 mm, die gap 0.8 mm. |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SAXAMID™ 136Q32 | SAX Polymers | Nylon 6 | SAXAMID™ |
| STARFLEX® P 7002 | STAR Thermoplastic Alloys & Rubbers, Inc. | TPE | STARFLEX® |
| Ecomann® Bioresin EM10080 | Shenzhen Ecomann Biotechnology Co., Ltd. | PHA | Ecomann® |
| Sylvin 6231-90 Yellow 4195 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 86021-70FUV White 1533 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |