SCHULAMID® 66 SK 1000
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IMHMh5_SCHULAMID-66-SK-1000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Extrem high impact Polyamide 66 |
| General Information | |
|---|---|
| Features |
|
| UL File Number |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.06 | -- | g/cm³ | ISO 1183/A |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.0 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 1800 | 600 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 50.0 | 30.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 6.0 | 32 | % | ISO 527-2/1A/50 |
| Nominal Tensile Strain at Break | > 40 | > 100 | % | ISO 527-2/1A/50 |
| Flexural Modulus 1 | 1650 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 62.0 | -- | MPa | ISO 178 |
| Flexural Strain at Flexural Strength | 7.0 | -- | % | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 25 | -- | kJ/m² | |
| 23°C | 80 | 120 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | -- | ||
| 23°C | No Break | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 135 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 60.0 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | ||||
| -- | > 250 | -- | °C | ISO 306/A50 |
| -- | 175 | -- | °C | ISO 306/B50 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate (2.00 mm) | 38 | -- | mm/min | ISO 3795 |
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 1.50 mm | HB | -- | ||
| 3.00 mm | HB | -- | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 1.50 mm | -- | 600 | °C | |
| 3.00 mm | -- | 600 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shinko-Lac® ASA S511 | Mitsubishi Rayon America Inc. | ASA | Shinko-Lac® |
| Wah Hong BMC 4122C | Wah Hong Industrial Corp. | TS, Unspecified | Wah Hong BMC |
| Celcon® M25 | Celanese Corporation | Acetal (POM) Copolymer | Celcon® |
| Fainplast PVC HGKA 79/R | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Sylvin 83048-85 Black | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |