Perfactory® RC25
| Category: | Unspecified , Unspecified |
| Manufacturer: | EnvisionTEC, Inc. |
| Trademark: | Perfactory® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IM1pYx_Perfactory-RC25.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
The EnvisionTEC RC25 is a high temperature resistant resin for building tough and stiff parts. RC25 is a nanoparticle filled material that is used to build hard-wearing, stiff and high temperature resistant parts. They have an opaque peach color appearance. Applications Aerospace, Animation and Entertainment, Architecture and Art, Automotive, Consumer Packaged Goods, Education, Electronics, Manufacturing, Sporting Goods, Toys Cleaning, drying and post curing is to be carried out as described in EnvisionTEC´s postprocessing instructions for this material. Recommendation: use incubator. Post curing of parts in Otoflash with 4,000 flashes. Recommended Machines: Perfactory® 4 Standard with ERM, Perfactory® 4 Standard XL with ERM |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Water Absorption (Equilibrium) | 0.25 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 93 | ASTM D1004 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4890 | MPa | ASTM D638 |
| Tensile Strength | 46.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.5 | % | ASTM D638 |
| Flexural Modulus | 3860 | MPa | ASTM D790 |
| Flexural Strength | 102 | MPa | ASTM D790 |
| Compressive Modulus | 4490 | MPa | ASTM D695 |
| Compressive Strength | < 127 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 16.0 | J/m² | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 67.0 | °C | |
| 1.8 MPa, Unannealed | 53.6 | °C | |
| Glass Transition Temperature | 42.0 | °C | ASTM E1545 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VINIKA® T133D | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Rigid | VINIKA® |
| 3M™ Dyneon™ PTFE Compound TF 6406 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |
| Haysite BMC 20000 | Haysite Reinforced Plastics | Polyester, TS | Haysite BMC |
| KOPELEN JM-370S | Lotte Chemical Corporation | PP Impact Copolymer | KOPELEN |
| Sylvin 5210-75 Green 3187 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |