Category: | Nylon 66 , Polyamide 66 |
Manufacturer: | Polykemi AB |
Trademark: | SCANAMID 66 |
Fillers: | - |
Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
Delivery Terms | FOB, CIF, DAP, DAT, DDP |
PDF: | ILOhS7_SCANAMID-66-A12-F25.pdf ![]() |
PRICE: | Order Products email sales@su-jiao.com |
Message |
---|
Glass fibre reinforced |
General Information | |
---|---|
Filler / Reinforcement |
|
Physical | Dry | Conditioned | Unit | Test Method |
---|---|---|---|---|
Density | 1.32 | -- | g/cm³ | ISO 1183 |
Molding Shrinkage | ISO 294-4 | |||
Across Flow | 1.0 | -- | % | |
Flow | 0.40 | -- | % |
Mechanical | Dry | Conditioned | Unit | Test Method |
---|---|---|---|---|
Tensile Stress | 155 | 130 | MPa | ISO 527-2 |
Tensile Strain (Yield) | 4.0 | 6.0 | % | ISO 527-2 |
Flexural Modulus (23°C) | 8000 | 5500 | MPa | ISO 178 |
Flexural Stress | 220 | 155 | MPa | ISO 178 |
Impact | Dry | Conditioned | Unit | Test Method |
---|---|---|---|---|
Charpy Notched Impact Strength | ISO 179 | |||
-20°C | -- | 8.0 | kJ/m² | |
23°C | 8.0 | 11 | kJ/m² | |
Charpy Unnotched Impact Strength | ISO 179 | |||
-20°C | -- | 25 | kJ/m² | |
23°C | 30 | 40 | kJ/m² |
Thermal | Dry | Conditioned | Unit | Test Method |
---|---|---|---|---|
Heat Deflection Temperature 1 | ||||
0.45 MPa, Unannealed | 250 | -- | °C | ISO 75-2/B |
1.8 MPa, Unannealed | 250 | -- | °C | ISO 75-2/A |
Vicat Softening Temperature | > 230 | -- | °C | ISO 306/B50 |
Flammability | Dry | Conditioned | Unit | Test Method |
---|---|---|---|---|
Flame Rating (1.60 mm) | HB | -- | UL 94 | |
Glow Wire Ignition Temperature (2.00 mm) | 650 | -- | °C | IEC 60695-2-13 |
Note Message | |
---|---|
1 . | 120°C/hr |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
Arlon® 1260 | Greene, Tweed & Co. | PEEK | Arlon® |
Geon™ Vinyl Dry Blend E0100 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Dry Blend |
INEOS PP H20Z-00 | INEOS Olefins & Polymers USA | PP Homopolymer | INEOS PP |
OmniPro™ HPP CCF10 | OMNI Plastics, LLC | PP Homopolymer | OmniPro™ |
SCHULAMID® RD 6 GF 30 | A. Schulman Europe | Nylon 6 | SCHULAMID® |