ELITE™ AT 6111
| Category: | EPE , Enhanced Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | ELITE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IKIC8o_ELITE-AT-6111.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ELITE™ AT 6111 Enhanced Polyethylene Resin is an ethylene-octene copolymer based on ELITE™ AT technology from Dow. This resin is designed for cast stretch machine wrap films in pallet wrap application and offers an optimized balance of extensibility, impact strength, and puncture resistance. Main Characteristics:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.912 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.7 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 20 | µm | |
| Film Puncture Energy (20 µm) | 2.87 | J | Internal method |
| Film Puncture Force (20 µm) | 36.9 | N | Internal method |
| Film Puncture Resistance (20 µm) | 23.0 | J/cm³ | Internal method |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 20 µm | 6.37 | MPa | ASTM D882 |
| TD : Yield, 20 µm | 6.30 | MPa | ASTM D882 |
| MD : Break, 20 µm | 44.3 | MPa | ASTM D882 |
| TD : Break, 20 µm | 38.1 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 20 µm | 440 | % | ASTM D882 |
| TD : Break, 20 µm | 560 | % | ASTM D882 |
| Dart Drop Impact (20 µm) | 740 | g | ASTM D1709A |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 20 µm | 240 | g | ASTM D1922 |
| TD : 20 µm | 470 | g | ASTM D1922 |
| Final stretch- On-Pallet testing 2(20.3 µm) | 300 | % | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature (DSC) | 109 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 20.3 µm) | 90 | ASTM D2457 | |
| Haze (20.3 µm) | 1.3 | % | ASTM D1003 |
| Extrusion instructions |
|---|
| Fabrication Conditions For Cast Film: EGAN/Davis-Standard 5 layer cast line Melt Temperature: 520°F (271°C) Chill Roll (primary/secondary) Temperature: 70°F (21°C) Line Speed: 600 fpm (183m/min) Output: 400 lb/hr Die Width: 36in. (915 mm) Die Gap: 20mil (0.5mm) Air Gap: 3in. (7.6mm) |
| Note Message | |
|---|---|
| 1 . | Method B |
| 2 . | Determined by Highlight Industries, Inc. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tarnamid® T- 27 CF20 | Grupa Azoty S.A. | Nylon 6 | Tarnamid® |
| VAMPORAN 0024 V1 13 | Vamp Tech | PPE+PS | VAMPORAN |
| Fiberfil® PP-60/TC/40 | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| Formolene® 6501A | Formosa Plastics Corporation, U.S.A. | PP Impact Copolymer | Formolene® |
| Globalene® ST861 | Lee Chang Yung Chemical Industry Corp. | PP Random Copolymer | Globalene® |