Innothane® IE-70DBS
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | Innothane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IK6DVQ_Innothane-IE-70DBS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| IE-70DBS is a 70 shore D polyurethane formulated for room temperature hand-batch processing. Excellent physical properties can be obtained with a room temperature cure without the utilization of mercury, MOCA, or TDI. |
| General Information | |
|---|---|
| RoHS Compliance |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Hardener | 1.05 | g/cm³ | |
| Cured | 1.10 | g/cm³ | |
| Base Resin | 1.12 | g/cm³ | |
| Molding Shrinkage - Flow | 0.10 | % | ASTM D2566 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 1720 | MPa | ASTM D790 |
| Flexural Strength | 62.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 27 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 60.0 | °C | ASTM D648 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 53 Mix Ratio by Weight: 50 | ||
| Resin | Mix Ratio by Weight: 100 Mix Ratio by Volume: 100 | ||
| Demold Time | 960 to 1400 | min |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 25°C 1 | 0.045 | Pa·s | |
| 25°C 2 | 0.20 | Pa·s | |
| 25°C 3 | 0.80 | Pa·s | |
| Curing Time (25°C) | 1.7E+2 | hr | |
| Gel Time | 1.2E+2 to 2.4E+2 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 65 to 75 | ASTM D2240 | |
| Tensile Strength | 27.6 | MPa | ASTM D638 |
| Tensile Elongation at Break | 4.0 | % | ASTM D638 |
| Note Message | |
|---|---|
| 1 . | Resin |
| 2 . | Mixed |
| 3 . | Hardener |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vi-Chem PVC VNC90 | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| Unichem 8300 | Colorite Polymers | PVC, Unspecified | Unichem |
| Urochem 161 | Chemiplastica, Inc. | Urea Formald | Urochem |
| ADEKA EH-5030S | Adeka Corporation | Epoxy | ADEKA |
| ALCOM® PA66 910/1.1 CF30 PTFE15 | ALBIS PLASTIC GmbH | Nylon 66 | ALCOM® PA66 |