Latilub 57-30GRTS G/20
| Category: | PPA , Polyphthalamide |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latilub |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IIdgtX_Latilub-57-30GRTS-G-20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Self-lubricating product based on Semi-aromatic polyammide (PPA). Glass fibres. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.54 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 1.2 to 1.6 | % | |
| Flow : 2.00 mm | 0.50 to 0.80 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 11000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 115 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 1.5 | % | ISO 527-2/5 |
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic | 0.22 | ||
| vs. Itself - Static | 0.24 | ||
| Wear Factor | 80 | 10^-8 mm³/N·m | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 20 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 295 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 275 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 245 | °C | ISO 306/B50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 130 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 310 to 330 | °C | |
| Mold Temperature | 150 to 170 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 60 MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirathane™ M80 | Miracll Chemicals Co., Ltd. | TPU-Polyether | Mirathane™ |
| Sylvin 9266-70 Grey 9517 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Cellidor B 631-12 | ALBIS PLASTIC GmbH | CAB | Cellidor |
| Hostacom 62F4-2C | LyondellBasell Industries | PP Homopolymer | Hostacom |
| Latan 13 S/30 | LATI S.p.A. | Acetal (POM) Copolymer | Latan |