SABIC® HDPE F00851
| Category: | HDPE, HMW , High Density (HMW) Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IHV4x7_SABICHDPEF00851.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® HDPE F00851 is a high molecular weight, high density polyethylene copolymer grade typically used for blown film applications. SABIC® HDPE F00851 typically offers a good balance between toughness and stiffness, good impact properties with low gel level. Typical applications SABIC® HDPE F00851 is typically used for blown film extrusion. Typical applications are heavy duty bags, grocery sacks, shopping bags, refuse bags, thin film for bag on roll and wrapping film. The grade can also be blended with LLDPE and LDPE and can be used in co-extrusion process. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.952 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/21.6 kg | 9.0 | g/10 min | ISO 1133 |
| 190°C/5.0 kg | 0.30 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 62 | ISO 868 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 20 | µm | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 20 µm, blown film | 50.0 | MPa | ISO 527-3 |
| TD : Yield, 20 µm, blown film | 45.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 20 µm, blown film | 400 | % | ISO 527-3 |
| TD : Broken, 20 µm, blown film | 450 | % | ISO 527-3 |
| Dart Drop Impact 1(20 µm, Blown Film) | 240 | g | ASTM D1709 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -80.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 75.0 | °C | ISO 306/B |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 2 | ISO 6383-2 | ||
| MD : 20.0 µm | 200.0 | kN/m | ISO 6383-2 |
| TD : 20.0 µm | 450.0 | kN/m | ISO 6383-2 |
| Film properties have been measured at 20 µm blown film with a BUR = 4. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 200 - 225 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SFN10010 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| UNITIKA Nylon 66 BV2120G15 | UNITIKA Plastics Division | Nylon 66 | UNITIKA Nylon 66 |
| Glastic® UTS 141 | Glastic Corporation | Polyester, TS | Glastic® |
| Karina IVORY PVC COMPOUND 550D35/ 1-AT-IS (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOCOMP™ QF007 compound | SABIC Innovative Plastics | Nylon 610 | LNP™ THERMOCOMP™ |