Flexathene® TP4310HR
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Flexathene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IHUFXQ_Flexathene-TP4310HR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FLEXATHENE TP4310HR is a thermoplastic polyolefin (TPO) formulated for compounding and injection molding applications that require medium stiffness and excellent cold temperature impact resistance. TP4310HR is produced in a proprietary gas-phase process that yields a product with greater resistance to mechanical and thermal degradation and more uniform dispersion than melt-blended rubber compounds. This product is readily reprocessible with minimal changes to processing characteristics or physical properties. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.895 | g/cm³ | ISO 1183/A, ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | |||
| 230°C/2.16 kg | 9.5 | g/10 min | ASTM D1238 |
| 230°C/2.16 kg 1 | 9.5 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 66 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1000 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield 2 | 19.3 | MPa | ASTM D638 |
| -- | 17.0 | MPa | ISO 527-2 |
| Tensile Elongation (Yield) | 5.5 | % | ASTM D638 |
| Flexural Modulus | |||
| 1% Secant 3 | 689 | MPa | ASTM D790B |
| -- | 700 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 43 | J/m | |
| -18°C | 110 | J/m | |
| 23°C | No Break | ||
| Unnotched Izod Impact (-18°C) | No Break | ASTM D4812 | |
| Instrumented Dart Impact 4 | ASTM D3763 | ||
| -40°C, Energy to Peak Load | 27.0 | J | |
| 23°C, Energy to Peak Load | 16.0 | J | |
| Gardner Impact (-30°C) | 27.1 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 70.0 | °C | ASTM D648 |
| Brittleness Temperature | -33.9 | °C | ASTM D746 |
| CLTE - Flow | 1.2E-4 | cm/cm/°C | ASTM E831 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 210 to 232 | °C |
| Note Message | |
|---|---|
| 1 . | Procedure A |
| 2 . | 13 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 2.20 m/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMOLAST® K TF9CGT (Series: FC) | KRAIBURG TPE | TPE | THERMOLAST® K |
| ALTECH® PP-H A 2030/250 GF30 CP | ALBIS PLASTIC GmbH | PP Homopolymer | ALTECH® PP-H |
| EBAC® SP1802 | Westlake Chemical Corporation | EnBA | EBAC® |
| LG PS 25SP(E) | LG Chem Ltd. | PS (GPPS) | LG PS |
| LUVOTECH® GS 46 | Lehmann & Voss & Co. | Nylon 46 | LUVOTECH® |