TRIREX® 3025U(400)

Category:	PC , Polycarbonate
Manufacturer:	Samyang Corporation
Trademark:	TRIREX®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	IGvmq5_TRIREX-3025U-400-.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

TRIREX 3025U(400) is a polycarbonate resin grade which has high low temperature impact strength in combination with superior mechanical and physical property.

Characteristics:

Superior low temperature impact resistance

Good flow-ability

Workable under a wide range of temperatures (-100 °C ~ 135 °C)

High electrical performance

Good dimensional stability

Low moisture absorbency

Good weather resistance

Applications:

TRIREX 3025U(400) resin grade is used for UV cut-off up to 400nm.

Medium viscosity. Transparent colors only.

General Information
Features	Good Dimensional Stability Good Electrical Properties Good Flow Good Weather Resistance Low Moisture Absorption Low Temperature Impact Resistance Medium Viscosity
Uses	Appliances Automotive Applications Electrical/Electronic Applications Optical Applications
Appearance	Clear/Transparent
Processing Method	Injection Molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.20	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (300°C/1.2 kg)	8.0	g/10 min	ASTM D1238
Water Absorption (24 hr)	0.15	%	ASTM D570

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (Yield)	70.1	MPa	ASTM D638
Tensile Elongation (Break)	140	%	ASTM D638
Flexural Modulus	2260	MPa	ASTM D790
Flexural Strength (Yield)	91.2	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (23°C, 3.18 mm)	930	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Unannealed)	134	°C	ASTM D648
CLTE - Flow	5.0E-5 to 7.0E-5	cm/cm/°C	ASTM D696

Electrical	Nominal Value	Unit	Test Method
Volume Resistivity	4.0E+16	ohms·cm	ASTM D257
Dielectric Strength	30	kV/mm	ASTM D149
Arc Resistance	120	sec	ASTM D495

Flammability	Nominal Value	Unit	Test Method
Flame Rating (1.59 mm)	V-2		UL 94

Optical	Nominal Value	Unit	Test Method
Haze	0.40	%	ASTM D1003

Injection	Nominal Value	Unit
Drying Temperature	120	°C
Drying Time	3.0 to 5.0	hr
Suggested Max Moisture	< 0.020	%
Rear Temperature	235 to 260	°C
Middle Temperature	250 to 275	°C
Front Temperature	265 to 290	°C
Nozzle Temperature	265 to 300	°C
Processing (Melt) Temp	265 to 300	°C
Mold Temperature	65.0 to 105	°C
Back Pressure	0.250 to 0.700	MPa
Screw Speed	40 to 70	rpm
Vent Depth	0.020 to 0.080	mm

Resin Grade	Manufacturer	Category	Trademark
Manner Flexible PVC X3484	Manner Plastics, L.P.	PVC, Flexible	Manner Flexible PVC
TEKNILID 1208	Tekni-Films, a div of Tekni-Plex	Film, Coated Al Foil	TEKNILID
Ferro PP LPP40YR01GY	Ferro Corporation	PP Copolymer	Ferro PP
Iupiace® AP4GM6	Mitsubishi Engineering-Plastics Corp	PPE+PS	Iupiace®
Sylvin 6224-85 Clear 8411	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin