LG ABS XG568
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | LG ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IGDcWO_LG-ABS-XG568.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LG ABS XG568 is an Acrylonitrile Butadiene Styrene (ABS) material. It is available in Asia Pacific, Europe, Latin America, or North America for injection molding. Important attributes of LG ABS XG568 are:
Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.11 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.20 to 0.40 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ASTM D570 |
| Moisture Content | > 0.010 | % |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Ozone Resistance 1 | No Crack | JIS K6301 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 114 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Yield, 3.20 mm) | 53.0 | MPa | ASTM D638 |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield, 3.20 mm | > 6.0 | % | |
| Break, 3.20 mm | 20 | % | |
| Flexural Modulus 4(3.20 mm) | 2750 | MPa | ASTM D790 |
| Flexural Strength 5(3.20 mm) | 85.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.20 mm | 39 | J/m | |
| -30°C, 6.40 mm | 39 | J/m | |
| 23°C, 3.20 mm | 88 | J/m | |
| 23°C, 6.40 mm | 88 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 86.0 | °C | |
| 0.45 MPa, Unannealed, 6.40 mm | 88.0 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 82.0 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 83.0 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 180 to 200 | °C | |
| Middle Temperature | 190 to 210 | °C | |
| Front Temperature | 200 to 220 | °C | |
| Nozzle Temperature | 200 to 230 | °C | |
| Processing (Melt) Temp | 200 to 230 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Back Pressure | 29.4 to 58.8 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5 sec |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 15 mm/min |
| 5 . | 15 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8828-74 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Unichem 8099 | Colorite Polymers | PVC, Unspecified | Unichem |
| BJB Silicone TC-5060 A/B | BJB Enterprises, Inc. | Silicone | BJB Silicone |
| EVICOM™ RC7/025 | INEOS Compounds | PVC, Rigid | EVICOM™ |
| InnoPlus HD2200JP | PTT Global Chemical Public Company Limited | HDPE | InnoPlus |