Ultramid® TG3S
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IG5zFW_Ultramid-TG3S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid TG3S is a 15% glass reinforced, heat stabilized, impact modified PA6 injection molding compound developed for applications requiring improved toughness in combination with a balance of strength, stiffness, excellent moldability and surface aesthetics. Applications It is generally recommended for application such as window hardware, wheel chairs wheels, bicycle wheels, power tool housings, hose clamps, clips and fasteners. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.21 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break, 23°C) | 90.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 3.5 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 4390 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 13 | kJ/m² | ISO 179 |
| Notched Izod Impact Strength | ISO 180 | ||
| -40°C | 5.4 | kJ/m² | |
| 23°C | 17 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 180 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 220 | °C | ISO 3146 |
| RTI Elec | UL 746 | ||
| 1.00 mm | 65.0 | °C | |
| 1.50 mm | 65.0 | °C | |
| 3.00 mm | 65.0 | °C | |
| RTI Imp | UL 746 | ||
| 1.00 mm | 65.0 | °C | |
| 1.50 mm | 65.0 | °C | |
| 3.00 mm | 65.0 | °C | |
| RTI Str | UL 746 | ||
| 1.00 mm | 65.0 | °C | |
| 1.50 mm | 65.0 | °C | |
| 3.00 mm | 65.0 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.00 mm | HB | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.080 | % | |
| Rear Temperature | 245 to 275 | °C | |
| Middle Temperature | 260 to 285 | °C | |
| Front Temperature | 270 to 295 | °C | |
| Nozzle Temperature | 270 to 295 | °C | |
| Processing (Melt) Temp | 270 to 295 | °C | |
| Mold Temperature | 80.0 to 95.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Zhongfa ABS FR-765 | Yuyao Zhongfa Engineering Plastics Co. Ltd. | ABS | Zhongfa |
| Braskem PP TI4900M | Braskem America Inc. | PP Impact Copolymer | Braskem PP |
| Geon™ Vinyl Dry Blend E6950 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Dry Blend |
| Kuraray Poval® PVA 105 | Kuraray Co., Ltd. | PVOH | Kuraray Poval® |
| RTP 2099 X 143509 B | RTP Company | Polyester Alloy | RTP |