Polifil® PE RP-HDPE
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | The Plastics Group |
| Trademark: | Polifil® PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IFwThf_Polifil-PE-RP-HDPE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polifil® RP-HDPE is a moderate stiffness material that retains excellent toughness. HDPE exhibits outstanding chemical resistance and environmental stress crack resistance. Injection molding applications range from small containers and lids to large crates and bins. Use this information as a guide to aid you in selecting the proper resin for your application. TPG will custom compound and fine-tune our formulations for your application. |
| General Information | |
|---|---|
| Recycled Content |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.958 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.10 to 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 2.8 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 64 | ASTM D1415 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1170 | MPa | ASTM D638 |
| Tensile Strength (23°C) | 24.1 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield, 23°C | 12 | % | |
| Break, 23°C | > 200 | % | |
| Flexural Modulus - Tangent (23°C) | 1030 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 27.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 85 | J/m | ASTM D256 |
| Gardner Impact (23°C, 12.7 mm) | > 22.6 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 71.1 | °C | |
| 1.8 MPa, Unannealed | 32.2 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PP GP3403 | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| Moplen EP380T | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| Nypol® PA B3 G63 HS PRTA012 NT380 | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |
| Carbotex KG-10MRA | Kotec Corporation | PC | Carbotex |
| Sylvin 2900-80 Clear 8391 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |