Castalloy™ 7126
| Category: | TS, Unspecified , Thermoset, Unspecified |
| Manufacturer: | Hapco Inc. |
| Trademark: | Castalloy™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IFbP0d_Castalloy-7126.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CASTALLOY is a series of fast, tough, low viscosity, very low cost, easy to use Liquid Molding Compounds. CASTALLOY has a short cycle time, providing a high volume of parts per day, ideal for both prototype and production runs. Fast turnover and very low cost are two key attributes of CASTALLOY. CASTALLOY has excellent physical properties such as: tensile strength, HDT, modulus of elasticity, etc. Parts can be de-molded in as little as 5 minutes! CASTALLOY can be used with silicone, epoxy, urethane, polyester, or aluminum molds. CASTALLOY is available in a creamy, off white color. Custom Coloring can be achieved by pigmenting CASTALLOY with Hapco's easy to mix color dispersions. CASTALLOY fills the need for low cost, high performance parts in virtually any industry. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D4669 |
| Molding Shrinkage - Flow | 0.20 to 0.50 | % | ASTM D2566 |
| Weight - per cubic inch | 17 | g |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gel Time 1(25°C) | 1.5 | min | ASTM D2971 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 72 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1550 | MPa | ASTM D638 |
| Tensile Strength | 33.9 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 5.6 | % | ASTM D638 |
| Flexural Modulus | 1450 | MPa | ASTM D790 |
| Flexural Strength | 64.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 15 | J/m | ASTM D256 |
| Unnotched Izod Impact | 74 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 102 | °C | |
| 1.8 MPa, Unannealed | 100 | °C |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100, Mix Ratio by Volume: 100 | ||
| Part B | Mix Ratio by Weight: 89, Mix Ratio by Volume: 100 | ||
| Thermoset Mix Viscosity (25°C) | 120 | cP | ASTM D4878 |
| Demold Time (21°C) | 10 to 12 | min | |
| Post Cure Time (66°C) | 6.0 to 8.0 | hr |
| Note Message | |
|---|---|
| 1 . | 100 g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravalene CR M 4544 | Ravago Group | MDPE | Ravalene |
| Telcar® TL-3260-1 | Teknor Apex Company | TPE | Telcar® |
| Versaflex™ OM 6160-9 | PolyOne Corporation | TPE | Versaflex™ |
| LNP™ STAT-KON™ RE006 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ STAT-KON™ |
| Kanghui KH2110 | Yingkou Kanghui Petrochemical Co., LTD. | PBT | Kanghui |