Kingfa FRABS-518
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Kingfa |
| Trademark: | Kingfa |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IF5dl6_Kingfa-FRABS-518.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Kingfa FRABS-518 is an acrylonitrile butadiene styrene (ABS) material,. This product is available in North America or Asia Pacific region. The processing method is injection molding. The main features of Kingfa FRABS-518 are:
the typical application fields of Kingfa FRABS-518 are: tools |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 200°C/5.0 kg | 2.5 | g/10 min | ASTM D1238 |
| 220°C/10.0 kg | 28 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (23°C) | 0.40 - 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 98 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 38.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 20 | % | ASTM D638 |
| Flexural Modulus 3 | 2000 | MPa | ASTM D790 |
| Flexural Strength 4 | 58.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 6.40 mm | 160 | J/m | ASTM D256 |
| 23°C, 3.20 mm | 340 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 87.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 77.0 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 95.0 | °C | ASTM D1525 5 |
| -- | 86.0 | °C | ASTM D1525 6 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | 23 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | UL 94 | |
| 3.00 mm | V-0 | UL 94 | |
| 2.00 mm | 5VB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 160 - 180 | °C | |
| Middle Temperature | 170 - 190 | °C | |
| Front Temperature | 180 - 210 | °C | |
| Processing (Melt) Temp | 170 - 210 | °C | |
| Mold Temperature | 30.0 - 60.0 | °C | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 0.00 - 0.0100 | MPa |
| Injection instructions |
|---|
| Processing Temperature Limit: 230°C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 标准 B (120°C/h), 压 力1 (10N) |
| 6 . | 速率 A (50°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 2952-70 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| TAROLON 2020 | Taro Plast S.p.A. | PC | TAROLON |
| Texalan® 7 Series 798A | Austin Novel Materials Co. Ltd. | TPU Alloy | Texalan® 7 Series |
| SIBUR Synthetic Rubber DST-30-01 | SIBUR | SBC | SIBUR Synthetic Rubber |
| Panlite® K-1285ZH | TEIJIN LIMITED | PC | Panlite® |