LNP™ STAT-LOY™ N30009 compound
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-LOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IEkG0g_LNPSTATLOYN30009compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-LOY* N30009 is a compound based on PC+ABS Blend resin containing Flame Retardant. Added features include: Permanent Antistatic, Flame Retardant. Also known as: LNP* STAT-LOY* Compound STATLOY-PCA-FR Product reorder name: N30009 |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.25 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.50 - 0.70 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 45.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | > 10 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 1700 | MPa | ISO 178 |
| Flexural Stress | 55.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 2(23°C) | 15 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3(1.8 MPa, Unannealed, 64.0 mm Span) | 100 | °C | ISO 75-2/Af |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+9 - 1.0E+11 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 210 - 230 | °C | |
| Middle Temperature | 210 - 221 | °C | |
| Front Temperature | 240 - 260 | °C | |
| Nozzle Temperature | 250 - 260 | °C | |
| Processing (Melt) Temp | 225 - 270 | °C | |
| Mold Temperature | 40.0 - 50.0 | °C | |
| Back Pressure | 0.200 - 0.300 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Medalist® MD-150 | Teknor Apex Company | TPE | Medalist® |
| Daelim Po1y® HX100S | DAELIM INDUSTRIAL CO., LTD. | HDPE | Daelim Po1y® |
| DENKA Transparent Polymer TH-21 | Denka Company Limited | MMBS | DENKA Transparent Polymer |
| Isocor™ 4011 | Shakespeare Monofilaments and Specialty Polymers | Nylon 6/69 | Isocor™ |
| LNP™ LUBRICOMP™ DX96651 compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |