Rotec® AES A 707
| Category: | AES , Acrylonitrile Ethylene Styrene |
| Manufacturer: | ROMIRA GmbH |
| Trademark: | Rotec® AES |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IBfA4c_Rotec-AES-A-707.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Rotec®AES A 707 is an acrylonitrile ethylene styrene (AES) material,. This product is available in Europe and is processed by extrusion or injection molding. Rotec®The main characteristics of AES A 707 are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.02 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 6.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.50 - 0.70 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1200 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 18.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | 42 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 1200 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 33.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 32 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 91.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Suggested Max Regrind | 5 | % | |
| Rear Temperature | 210 - 250 | °C | |
| Middle Temperature | 210 - 250 | °C | |
| Front Temperature | 210 - 250 | °C | |
| Processing (Melt) Temp | < 260 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Injection Rate | Fast |
| Injection instructions |
|---|
| Screw rotation speed: moderate to highBack pressure: low to moderateInjection pressure: tool depending |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Cylinder Zone 1 Temp. | 190 - 210 | °C | |
| Cylinder Zone 2 Temp. | 190 - 210 | °C | |
| Cylinder Zone 3 Temp. | 190 - 210 | °C | |
| Cylinder Zone 4 Temp. | 190 - 210 | °C | |
| Cylinder Zone 5 Temp. | 190 - 210 | °C | |
| Melt Temperature | < 245 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro-fax SL439 | INDELPRO, S.A. de C.V. | PP Random Copolymer | Pro-fax |
| RJM EC101 | RJM International, Inc. | PC | RJM |
| Spartech Polycom WJ8341FR-105 | Spartech Polycom | PVC Alloy | Spartech |
| LNP™ THERMOCOMP™ CX05470 compound | SABIC Innovative Plastics | PS (HIPS) | LNP™ THERMOCOMP™ |
| LNP™ THERMOCOMP™ JF004Z compound | SABIC Innovative Plastics Europe | PESU | LNP™ THERMOCOMP™ |