Celanex® 1662Z
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Celanese Corporation |
| Trademark: | Celanex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IBHA34_Celanex1662Z.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Celanex 1662Z is a 30% glass reinforced polybutylene terephthalate with a good balance of mechanical properties and processability |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.52 | g/cm³ | ASTM D792 |
| -- | 1.53 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 7.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage | |||
| Flow | 2.0 - 6.0 | % | ASTM D955 |
| Flow | 0.30 - 0.50 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 90 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9200 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Fracture, 23°C | 124 | MPa | ASTM D638 |
| Fracture | 130 | MPa | ISO 527-2/1A/5 |
| Tensile Elongation | |||
| Fracture, 23°C | 4.0 | % | ASTM D638 |
| Fracture | 3.1 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 9700 | MPa | ISO 178 |
| Flexural Stress (23°C) | 210 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 11 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 12 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 221 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 225 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 208 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 205 | °C | ISO 75-2/A |
| Melting Temperature 1 | 225 | °C | ISO 11357-3, ASTM D3418 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 1.9E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength 2 | 21 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.8 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 130 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 230 - 240 | °C | |
| Middle Temperature | 235 - 250 | °C | |
| Front Temperature | 235 - 250 | °C | |
| Nozzle Temperature | 250 - 260 | °C | |
| Processing (Melt) Temp | 235 - 260 | °C | |
| Mold Temperature | 65 - 93 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.00 - 0.345 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 250 to 260°CZone 4 Temperature: 240 to 260°CFeed Temperature: 230 to 240°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1083 | RTP Company | PBT | RTP |
| Scolefin 13 G 10-9 | Ravago Group | PP Homopolymer | Scolefin |
| NILENE® E K30T | Taro Plast S.p.A. | PP Copolymer | NILENE® |
| KumhoSunny PPO HPP8430G | Shanghai KumhoSunny Plastics Co., Ltd. | PPE+PS | KumhoSunny PPO |
| MTEGRITY™ LLDPE LL204AA | M. Holland Company | LLDPE | MTEGRITY™ LLDPE |