3M™ Dyneon™ TFM™ Modified PTFE Compound TFM 4215
| Category: | PTFE , Polytetrafluoroethylene |
| Manufacturer: | 3M Advanced Materials Division |
| Trademark: | 3M™ Dyneon™ TFM™ Modified PTFE Compound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IADEgO_3M-Dyneon-TFM-Modified-PTFE-Compound-TFM-4215.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 3M™ Dyneon™ TFM™ Modified PTFE Compound 4215 is a Polytetrafluoroethylene (PTFE) product filled with 25% carbon fiber. It can be processed by compression molding or sintering and is available in Europe or North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 2.11 | g/cm³ | ASTM D4745-06 |
| Apparent Density | 0.72 | g/cm³ | ASTM D4894 |
| Molding Shrinkage - Flow | 3.1 | % | ASTM D4894-07 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness 1(Shore D) | 72 | DIN 53505 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Break) | 15.0 | MPa | ASTM D4745-06 |
| Tensile Elongation 3(Break) | 70 | % | ASTM D4745-06 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Compression Molding Molding Pressure | 80.0 | MPa | |
| Compression Molding Temperature | 23 to 26 | °C | |
| Sintering Temperature | < 365 | °C |
| Note Message | |
|---|---|
| 1 . | Measured on sintered moldings |
| 2 . | Measured on sintered moldings |
| 3 . | Measured on sintered moldings |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P2635 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| TUFNYL® SGF 25 NATURAL | SRF Ltd. | Nylon 6 | TUFNYL® |
| Bayblend® T45 PG | Covestro - Polycarbonates | PC+ABS | Bayblend® |
| CompaMid® PA 6.6 GF 30 HI | DimeLika Plast GmbH | Nylon 66 | CompaMid® |
| NORYL™ 731 resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |