| Solef® 60512 PVDF copolymer has high viscosity of the melt and it is a grade for offshore piping. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.75 to 1.80 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/10.0 kg) | 2.5 to 4.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 2.0 to 3.0 | % | |
| Water Absorption (23°C, 24 hr) | < 0.040 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 2.00 mm) | 70 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(23°C, 2.00 mm) | 1250 to 1400 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield, 23°C, 2.00 mm | 34.0 to 40.0 | MPa | |
| Break, 23°C, 2.00 mm | 34.0 to 40.0 | MPa | |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield, 23°C, 2.00 mm | 9.0 to 12 | % | |
| Break, 23°C, 2.00 mm | 100 to 300 | % | |
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic | 0.20 to 0.30 | ||
| vs. Itself - Static | 0.20 to 0.40 | ||
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-10 Wheel) | 5.00 to 10.0 | mg | ASTM D4060 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 4(23°C, 4.00 mm) | 1000 | J/m | ASTM D6110 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -40.0 | °C | ASTM D4065 |
| Vicat Softening Temperature | 167 | °C | ASTM D1525 5 |
| Melting Temperature | 170 to 174 | °C | ASTM D3418 |
| Peak Crystallization Temperature (DSC) | 142 to 146 | °C | ASTM D3418 |
| CLTE - Flow (0 to 40°C) | 1.3E-4 to 1.8E-4 | cm/cm/°C | ASTM D696 |
| Specific Heat | ASTM E968 | ||
| 23°C | 1200 | J/kg/°C | |
| 100°C | 1600 | J/kg/°C | |
| Thermal Conductivity (23°C) | 0.20 | W/m/K | ASTM C177 |
| Crystallization Heat | 42.0 to 50.0 | J/g | ASTM D3417 |
| Heat of Fusion | 41.0 to 50.0 | J/g | ASTM D3417 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+14 | ohms | ASTM D257 |
| Volume Resistivity | > 1.0E+14 | ohms·cm | ASTM D257 |
| Note Message | |
|---|---|
| 1 . | Type IV, 1.0 mm/min |
| 2 . | Type IV, 50 mm/min |
| 3 . | Type IV, 50 mm/min |
| 4 . | 2 m/s, Partial Break |
| 5 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wondel® B BG9F | Nanjing Julong Engineering Plastics Co., LTD | Nylon 6 | Wondel® B |
| DOMAMID® 28 | DOMO Caproleuna GmbH | Nylon 6 | DOMAMID® |
| Fluoroelastomer 931 | Greene, Tweed & Co. | Fluorelastomer | Fluoroelastomer |
| Elastron® G G100.D35.B | Elastron USA, Inc. | SEBS | Elastron® G |
| LUVOCOM® 70-9046 | LEHVOSS Group | PK | LUVOCOM® |