Badamid® PA610 GF50
| Category: | Nylon 610 , Polyamide 610 |
| Manufacturer: | Bada AG |
| Trademark: | Badamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | I9cAp3_Badamid-PA610-GF50.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Badamid® PA610 GF50 is a Polyamide 610 (Nylon 610) material filled with 50% glass fiber. It is available in Europe for injection molding. Primary attribute of Badamid® PA610 GF50: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.57 | -- | g/cm³ | ISO 1183 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.90 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 16300 | 15000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 240 | 200 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break, 23°C) | 2.5 | 3.0 | % | ISO 527-2/1A/5 |
| Flexural Stress (23°C, 4.00 mm) | 350 | 290 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 14 | -- | kJ/m² | |
| 23°C | 18 | -- | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 75 | -- | kJ/m² | |
| 23°C | 95 | -- | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 212 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 205 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) 1 | 220 | -- | °C | ISO 3146 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity (1.00 mm) | 1.0E+12 | -- | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 450 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | HB | -- | ||
| 1.60 mm | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 250 to 290 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 10 K/Min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makroblend® KU2-7912 | Covestro - Polycarbonates | PC+PBT | Makroblend® |
| CERTENE™ PBM-35 | Muehlstein | PP Impact Copolymer | CERTENE™ |
| Karina COMP. PVC BLACK -E KAPU 601-48/ 1 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Polifor® L6 GF/50 NATURALE | SO.F.TER. SPA | PP Homopolymer | Polifor® |
| LNP™ LUBRICOMP™ KL004A compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ LUBRICOMP™ |