LNP™ LUBRICOMP™ GL003 compound
| Category: | PSU , Polysulfone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | I9G6P5_LNPLUBRICOMPGL003compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP GL003 is a compound based on Polysulfone resin containing PTFE. Added features of this material include: Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound GL-4030 Product reorder name: GL003 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow | 0.76 | % | Internal method |
| Flow : 24 hours | 0.70 - 0.90 | % | ASTM D955 |
| Transverse flow | 0.83 | % | Internal method |
| Transverse flow : 24 hours | 0.70 - 0.90 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.83 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.76 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Fracture | 55.2 | MPa | ASTM D638 |
| Fracture 1 | 55.8 | MPa | ASTM D638 |
| Fracture | 55.0 | MPa | ISO 527-2, ISO 527-2/5 |
| Tensile Elongation | |||
| Fracture | 9.9 | % | ASTM D638 |
| Fracture 2 | 10 | % | ASTM D638 |
| Fracture | 12 | % | ISO 527-2, ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 3 | 2070 | MPa | ASTM D790 |
| -- | 2070 | MPa | ASTM D790 |
| -- | 2300 | MPa | ISO 178 |
| -- 4 | 2300 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 75.8 | MPa | ASTM D790 |
| -- | 79.0 | MPa | ISO 178 |
| -- | 79.0 | MPa | ISO 178 |
| Yield, 50.0mm span 5 | 82.2 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.23 | ASTM D3702 Modified | |
| With Self-Static | 0.13 | ASTM D3702 Modified | |
| Wear Factor - Washer | 24.5 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 59 | J/m | ASTM D256 |
| 23°C 6 | 6.1 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 890 | J/m | ASTM D4812 |
| 23°C 7 | 55 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 178 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 8 | 179 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 170 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 9 | 169 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 - 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 327 - 338 | °C | |
| Middle Temperature | 338 - 349 | °C | |
| Front Temperature | 349 - 360 | °C | |
| Processing (Melt) Temp | 360 - 371 | °C | |
| Mold Temperature | 149 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Type 1, 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 mm |
| 9 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 205 FR XB | RTP Company | Nylon 66 | RTP |
| Solarkote® P-601 | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Solarkote® |
| Sylvin 8437-76 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Arnite® TZ4 254 S | DSM Engineering Plastics | PBT | Arnite® |
| Colorite G Series 8312G-015 | Colorite Polymers | PVC, Flexible | Colorite G Series |