Radiflam® A RV350 AF 375 NER 4529
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Radici Plastics |
| Trademark: | Radiflam® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | I8mUPQ_Radiflam-A-RV350-AF-375-NER-4529.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PA66 flame retardant injection moulding grade with red phosphorus. 35% glass fiber reinforced. Improved impact properties. Black colour. Suitable for parts requiring fire retardancy along with good stiffness and mechanical resistance. Rated V-0 at 0.75 mm according to UL-94. ISO 1043 : PA66 GF35 FR(52) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| UL File Number |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.42 | -- | g/cm³ | ISO 1183 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 10100 | -- | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 130 | -- | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 3.2 | -- | % | ISO 527-2/1A/5 |
| Flexural Modulus 1 | 8800 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 200 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 70 | -- | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 225 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 240 | -- | °C | ISO 306/B50 |
| Melting Temperature 3 | 260 | -- | °C | ISO 11357 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 500 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate | 0.0 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | V-0 | -- | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 1.00 mm | 960 | -- | °C | |
| 2.00 mm | 960 | -- | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 1.00 mm | 725 | -- | °C | |
| 2.00 mm | 750 | -- | °C |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 80.0 | °C | |
| Drying Time - Desiccant Dryer | 2.0 to 4.0 | hr | |
| Dew Point - Desiccant Dryer | < -20.0 | °C | |
| Suggested Max Moisture | 0.10 | % | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Monprene® CP-18178 | Teknor Apex Company | TPE | Monprene® |
| Vi-Chem PVC VNC87-5E | Vi-Chem Corporation | PVC, Flexible | Vi-Chem PVC |
| Daelim Po1y® LL-24 | DAELIM INDUSTRIAL CO., LTD. | LLDPE | Daelim Po1y® |
| ExxonMobil™ HDPE HD 6706 Series | ExxonMobil Chemical | HDPE, UHMW | ExxonMobil™ HDPE |
| Karina GRAY PVC COMPOUND -E 830-18/ 99-CRM | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |