EL-Lene™ H5814J
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | SCG Chemicals Co., Ltd. |
| Trademark: | EL-Lene™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | I8kwLv_EL-Lene-H5814J.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EL-Lene H5814J is a general purpose high density polyethylene resin suitable for using in injection molding process. This good flowability grade designed for high productivity with good toughness product. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.958 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 14 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 2.00mm | 1.6 | % | ASTM D955 |
| Transverse flow : 2.00mm | 1.8 | % | ASTM D955 |
| Environmental Stress-Cracking Resistance (50°C, 25% Igepal, Compression Molded, F50) | 2.00 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 65 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 27.5 | MPa | ASTM D638 |
| Fracture | 17.7 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 620 | % | ASTM D638 |
| Flexural Modulus | 1230 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 29 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 75.0 | °C | ASTM D648 |
| Brittleness Temperature | -60.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 122 | °C | ASTM D1525 |
| Melting Temperature | 131 | °C | ASTM D2117 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 200 - 250 | °C | |
| Mold Temperature | 20.0 - 60.0 | °C | |
| Injection Rate | Fast | ||
| Screw Speed | 40 - 70 | rpm |
| Injection instructions |
|---|
| Injection Pressure: 30 to 70% of max. pressurePacking and Holding Pressure: 30 to 50% of max. pressureBack Pressure: 10% of max. pressure |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 385 TFE 20 | RTP Company | PC | RTP |
| Ultra Low Outgassing™ SCV-2585 | NuSil Technology | Silicone | Ultra Low Outgassing™ |
| Petrothene® NA362176 | LyondellBasell Industries | LDPE | Petrothene® |
| Sylvin 8215-75UV Blue 8451 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Silastic® Q7-4535 | Dow Corning Corporation | Silicone | Silastic® |