TECHNYL® B 218 MT25 V15 BLACK 21 N Datasheet,Nylon 66/6,Solvay Engineering Plastics-SHANGHAI SUSHENG

Message
TECHNYL® B 218 MT25 V15 Black 21N is a polyamide 66/6, reinforced with 25% of mineral filler and 15% of glass fibre, heat stabilized, for injection moulding.

General Information
Filler / Reinforcement	Glass \mineral, 40% filler by weight
Additive	heat stabilizer
Features	Heat Stabilized - Inorganic Low warpage Excellent appearance
Uses	Accessories Application in Automobile Field
Agency Ratings	EC 1907/2006 (REACH)
RoHS Compliance	RoHS compliance
Appearance	Black
Forms	Particle
Processing Method	Injection molding
Resin ID (ISO 1043)	PA66/6-MD25+GF15

Physical	Dry	Conditioned	Unit	Test Method
Density	1.47	--	g/cm³	ISO 1183/A
Water Absorption (23°C, 24 hr)	1.1	--	%	ISO 62

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus (23°C)	8500	4500	MPa	ISO 527-2/1A
Tensile Stress (Break, 23°C)	125	70.0	MPa	ISO 527-2/1A
Tensile Strain				ISO 527-2
Yield, 23°C	3.5	6.5	%	ISO 527-2
Fracture, 23°C	3.5	--	%	ISO 527-2
Flexural Modulus (23°C)	8100	3500	MPa	ISO 178

Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength (23°C)	3.5	5.5	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	45	80	kJ/m²	ISO 179/1eU
Notched Izod Impact (23°C)	3.8	6.0	kJ/m²	ISO 180

Thermal	Dry	Conditioned	Unit	Test Method
Melting Temperature	242	--	°C	ISO 11357-3

Electrical	Dry	Conditioned	Unit	Test Method
Surface Resistivity	5.0E+15	1.0E+12	ohms	IEC 60093
Volume Resistivity	1.0E+15	1.0E+14	ohms·cm	IEC 60093
Dielectric Strength (2.00 mm)	35	32	kV/mm	IEC 60243-1
Dissipation Factor	0.020	0.080		IEC 60250
Comparative Tracking Index (Solution A)	475	425	V	IEC 60112

Injection	Dry	Unit
Drying Temperature	80	°C
Suggested Max Moisture	0.20	%
Rear Temperature	255 - 265	°C
Middle Temperature	260 - 270	°C
Front Temperature	270 - 280	°C
Mold Temperature	70 - 100	°C

Injection instructions
The material is supplied in airtight bags, ready for use. In case that the virgin material has absorbed moisture, it must be dried with a dehumidified air drying equipment, dew point mini -20°C. Recommended time 2-4hInjection Advice: For reinforced polyamide, Solvay recommends the use of steel with a high content of Carbon and purified for polishing to avoid or limit the abrasion. For example: X38CrMoV5-1 (EN Norm) - 1.2367 /1.2343 (DIN Norm) or X160CrMoV12 (EN Norm) - 1.2601 /1.2379 (DIN Norm). For Mould Temperature, in the case of parts where the surface roughness is required we can recommend a temperature of 90°C to 120°C with an optimum at 105°C.

Injection instructions

The material is supplied in airtight bags, ready for use. In case that the virgin material has absorbed moisture, it must be dried with a dehumidified air drying equipment, dew point mini -20°C. Recommended time 2-4hInjection Advice: For reinforced polyamide, Solvay recommends the use of steel with a high content of Carbon and purified for polishing to avoid or limit the abrasion. For example: X38CrMoV5-1 (EN Norm) - 1.2367 /1.2343 (DIN Norm) or X160CrMoV12 (EN Norm) - 1.2601 /1.2379 (DIN Norm). For Mould Temperature, in the case of parts where the surface roughness is required we can recommend a temperature of 90°C to 120°C with an optimum at 105°C.

Category:	Nylon 66/6 , Polyamide 66/6 Copolymer
Manufacturer:	Solvay Engineering Plastics
Trademark:	TECHNYL®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	I7cBOg_TECHNYLB218MT25V15BLACK21N.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
POPELEN SRX-373	Lotte Chemical Corporation	PP Impact Copolymer	POPELEN
Primefin V500TL40HS	Lucent Polymers, Inc.	PP Homopolymer	Primefin
Elvax® 3128-1	DuPont Packaging & Industrial Polymers	EVA	Elvax®
Karina MBPEB WHITE-E 1000/6000-IE	Karina Ind. e Com. de Pl谩sticos Ltda	PVC, Unspecified	Karina
Lupolen 3220 F	LyondellBasell Industries	LDPE	Lupolen