Lupoy® 1080-70
| Category: | PC , Polycarbonate |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lupoy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | I7ZnzQ_Lupoy-1080-70.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LUPOY PC 1080-70 resin is designed for optical media discs applications. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 70 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Water Absorption | ASTM D570 | ||
| 23°C, 24 hr | 0.15 | % | |
| Equilibrium, 23°C, 50% RH | 0.32 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield, 23°C 1 | 60.0 | MPa | |
| Break | 48.0 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield | 6.0 | % | |
| Break | 60 | % | |
| Flexural Modulus | 2500 | MPa | ASTM D790 |
| Flexural Strength | 100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 2(23°C, 3.20 mm) | 270 | J/m | ASTM D256 |
| Instrumented Dart Impact 3(23°C, 3.20 mm, Total Energy) | 520 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Annealed, 4.00 mm | 137 | °C | |
| 1.8 MPa, Unannealed, 4.00 mm | 124 | °C | |
| Vicat Softening Temperature | 147 | °C | ASTM D1525 4 |
| CLTE - Flow (-40 to 82°C) | 6.8E-5 | cm/cm/°C | ASTM D696 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.583 | ASTM D542 | |
| Transmittance | 91.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 0.25 mm Notch Depth |
| 3 . | 3.38 m/sec |
| 4 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL PPX-GP2 | Polymer Resources Ltd. | PPE+PS | PRL |
| UNIGARD™ RE DFDA-1638 NT | The Dow Chemical Company | TP, Unspecified | UNIGARD™ |
| KOPA® KN333G15HI | Kolon Plastics, Inc. | Nylon 66 | KOPA® |
| Lucel® FW715CS | LG Chem Ltd. | Acetal (POM) Copolymer | Lucel® |
| Pearlthane® ECO D12T90 | Lubrizol Advanced Materials, Inc. | TPU, Unspecified | Pearlthane® ECO |