Exelene® LDPE 0700
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Montachem International, Inc. |
| Trademark: | Exelene® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | I7K2YR_Exelene-LDPE-0700.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Applications:
Characteristics:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.923 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.70 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Strength 1 | ASTM D882 | ||
| -- 2 | 221 | MPa | |
| -- 3 | 193 | MPa |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| Tensile Strength 4 | ASTM D882A | ||
| MD : Break | 33.1 | MPa | |
| TD : Break | 21.4 | MPa | |
| Tensile Elongation 5 | ASTM D882A | ||
| MD : Break | 200 | % | |
| TD : Break | 800 | % | |
| Dart Drop Impact 6(38000 µm) | 110 | g | ASTM D1709A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 110 | °C | DSC |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze | 4.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 5.1 mm/min |
| 2 . | TD, 1% secant |
| 3 . | MD, 1% secant |
| 4 . | 510 mm/min |
| 5 . | 510 mm/min |
| 6 . | F50, 66 cm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRANSMARE® 35HT40-0.001 | Transmare Compounding B.V. | PP Homopolymer | TRANSMARE® |
| Edistir® R 540E | Versalis S.p.A. | PS (HIPS) | Edistir® |
| Laprene® 83FM00A55 | SO.F.TER. SPA | SEBS | Laprene® |
| Paracril® 30.55XL | INSA | NBR | Paracril® |
| Durethan® B 35 F 000000 | LANXESS Corporation | Nylon 6 | Durethan® |