Generic PC+PBT - Glass Fiber
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | I6gy9b_Generic-PC-PBT---Glass-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PC+PBT - Glass Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.26 - 1.60 | g/cm³ | ASTM D792 |
| 23°C | 1.30 - 1.51 | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 - 0.80 | g/cm³ | ISO 60 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 23°C | 0.25 - 0.73 | % | ASTM D955 |
| Transverse flow : 23°C | 0.50 - 0.75 | % | ASTM D955 |
| Water Absorption | |||
| 23°C, 24 hr | 0.060 - 0.092 | % | ASTM D570 |
| Saturated, 23°C | 0.10 - 0.50 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.076 - 0.15 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 110 - 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 4400 - 12800 | MPa | ASTM D638 |
| 23°C | 4510 - 10200 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 83.3 - 105 | MPa | ASTM D638 |
| Fracture, 23°C | 105 - 132 | MPa | ASTM D638 |
| Fracture, 23°C | 73.0 - 101 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield, 23°C | 1.0 - 3.5 | % | ASTM D638 |
| Fracture, 23°C | 2.8 - 6.2 | % | ASTM D638 |
| Fracture, 23°C | 1.0 - 6.2 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 2860 - 8280 | MPa | ASTM D790 |
| 23°C | 3980 - 8920 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 77.2 - 187 | MPa | ASTM D790 |
| 23°C | 100 - 189 | MPa | ISO 178 |
| Yield, 23°C | 130 - 196 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.8 - 21 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 35 - 45 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 71 - 97 | J/m | ASTM D256 |
| 23°C | 7.9 - 10 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| 23°C | 590 - 640 | J/m | ASTM D256 |
| 23°C | 30 - 36 | kJ/m² | ISO 180 |
| Instrumented Dart Impact (23°C) | 6.50 - 8.30 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 139 - 216 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 133 - 212 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 107 - 210 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 95.0 - 192 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 121 - 192 | °C | ASTM D1525 |
| -- | 129 - 212 | °C | ISO 306 |
| Linear thermal expansion coefficient | |||
| Flow | 1.6E-5 - 2.4E-5 | cm/cm/°C | ASTM E831 |
| Flow | 2.0E-5 - 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 4.9E-5 - 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| RTI Elec | 75.0 - 140 | °C | UL 746 |
| RTI Imp | 75.0 - 130 | °C | UL 746 |
| RTI | 75.0 - 140 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 1.0 - 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength | |||
| 23°C | 19 - 29 | kV/mm | ASTM D149 |
| 23°C | 15 - 34 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 23°C | 3.48 - 4.00 | ASTM D150 | |
| 23°C | 3.49 | IEC 60250 | |
| Dissipation Factor (23°C) | 1.4E-3 - 0.020 | ASTM D150 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 - 121 | °C | |
| Drying Time | 3.0 - 6.1 | hr | |
| Drying Time, Maximum | 10 | hr | |
| Suggested Shot Size | 60 - 65 | % | |
| Rear Temperature | 242 - 261 | °C | |
| Middle Temperature | 244 - 266 | °C | |
| Front Temperature | 250 - 271 | °C | |
| Nozzle Temperature | 250 - 266 | °C | |
| Processing (Melt) Temp | 250 - 272 | °C | |
| Mold Temperature | 60.0 - 90.0 | °C | |
| Back Pressure | 0.448 - 0.517 | MPa | |
| Screw Speed | 53 - 65 | rpm | |
| Vent Depth | 0.017 - 0.032 | mm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PC+PBT - Glass FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP PP 10 GF | RTP Company | PP, Unspecified | RTP |
| TEKALOY™ G70A4 | Mando Advanced Materials Co., Ltd. | PC+ABS | TEKALOY™ |
| NEXUS PP RPP35C | Nexus Resin Group, LLC. | PP Random Copolymer | NEXUS PP |
| Grilamid® TR XE 4139 black 9231 | EMS-GRIVORY | Nylon, Unspecified | Grilamid® |
| Sylvin 8996-75 FU Brown 7260 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |