AVALON® 95 ABR
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Huntsman Corporation |
| Trademark: | AVALON® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | I6GEkU_AVALON-95-ABR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AVALON 95 ABR is a high performance polyester based thermoplastic polyurethane for injection moulding applications. AVALON 95 ABR is part of the AVALON Perform Range and offers a premium soling material for demanding applications where exceptional abrasion resistance is required such as soccer studs and sports cleats. The features offered include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.22 | g/cm³ | ISO 2781 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ISO 868 | ||
| Shaw A | 95 | ISO 868 | |
| Shaw D | 50 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus (23°C) | 80.0 | MPa | ISO 178 |
| Ross Flex 1(-10°C) | 2.5E+5 | Cycles | |
| Abrasion Resistance | 20.0 | mm³ | ISO 4649 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 37 | ||
| 100% strain | 13.0 | MPa | ISO 37 |
| 300% strain | 24.0 | MPa | ISO 37 |
| Tensile Stress (Break) | 35.0 | MPa | ISO 37 |
| Tensile Elongation (Break) | 430 | % | ISO 37 |
| Tear Strength 2 | 150 | kN/m | ISO 34-1 |
| Compression Set (23°C) | 20 | % | ISO 815 |
| Additional Information |
|---|
| Test plates conditioned 20 hours at 100°C before testing |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 80.0 - 90.0 | °C | |
| Drying Time - Desiccant Dryer | 2.0 | hr | |
| Hopper Temperature | 25.0 - 35.0 | °C | |
| Rear Temperature | 190 - 200 | °C | |
| Middle Temperature | 195 - 205 | °C | |
| Front Temperature | 200 - 210 | °C | |
| Nozzle Temperature | 185 - 195 | °C | |
| Mold Temperature | 25.0 - 50.0 | °C | |
| Injection Pressure | 2.00 - 10.0 | MPa | |
| Injection Rate | Slow | ||
| Holding Pressure | 1.00 - 5.00 | MPa | |
| Back Pressure | 0.0300 - 0.300 | MPa | |
| Screw Speed | 20 - 80 | rpm | |
| Screw L/D Ratio | 20.0:1.0 to 25.0:1.0 | ||
| Screw Compression Ratio | 2.0 : 1.0 - 3.0 : 1.0 |
| Injection instructions |
|---|
| Typical Screw Diameter : 40 - 120 mm3 Stage Design Feed Zone : 0.4L Compression Zone : 0.3L Metering Zone : 0.3L |
| Note Message | |
|---|---|
| 1 . | BS 5131 |
| 2 . | Method B, right-angle specimen (without cut) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® OBC 4955A | Teknor Apex Company | TPE | Telcar® |
| TECAMID™ GF30 | Ensinger Inc. | Nylon 66 | TECAMID™ |
| Wellamid® GS25-66 22L-NBK1 | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| Hostalen GM 5010 T3 S yellow | LyondellBasell Industries | HDPE | Hostalen |
| OTECH PVC OC5014-Boot | OTECH Corporation | PVC, Unspecified | OTECH PVC |