SD POLYCA™ CR3341T
| Category: | PBT+PC+PET , Polybutylene Terephthalate + PC + PET |
| Manufacturer: | Sumika Styron Polycarbonate Limited |
| Trademark: | SD POLYCA™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | I5kOIN_SDPOLYCACR3341T.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SD POLYCA CR series are PC/Polyester alloy grades. These products have improved chemical resistant property in addition to high impact property and heat resistant property of polycarbonate resin. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Part Marking Code |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.22 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (280°C/1.2 kg) | 6.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.60 - 0.80 | % | ASTM D955 |
| Transverse flow | 0.60 - 0.80 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.20 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 | MPa | ISO 527-2 |
| Tensile Strength | |||
| -- | 63.0 | MPa | ASTM D638 |
| -- | 62.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture | 130 | % | ASTM D638 |
| Fracture | 100 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2360 | MPa | ASTM D790 |
| -- | 2400 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 89.0 | MPa | ASTM D790 |
| -- | 95.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C) | 98 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 135 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 120 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 115 | °C | ISO 75-2/A |
| Linear thermal expansion coefficient | ASTM D696 | ||
| Flow | 7.0E-5 | cm/cm/°C | ASTM D696 |
| Lateral | 7.0E-5 | cm/cm/°C | ASTM D696 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance | 73.0 | % | ASTM D1003 |
| Haze | 42 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Propafilm™ RGR02/120 | Innovia Films Ltd. | PP Alloy | Propafilm™ |
| Sylvin 6214-90 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LEXAN™ HPS1 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| POLIMAXX 2300SC | IRPC Public Company Limited | PP Impact Copolymer | POLIMAXX |
| ULTEM™ HU1110 resin | SABIC Innovative Plastics | PEI | ULTEM™ |