Braskem PE F 7018
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | I5iuhI_Braskem-PE-F-7018.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
F7018 is a low density polyethylene that shows an excellent seal ability at low temperatures and indicated for low viscosity required applications. It does not contain additives. Application: Masterbatches; Extrusion coating; Injected parts. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.918 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 7.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 43 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, Compression Molded | 10.0 | MPa | |
| Break | 9.00 | MPa | |
| Flexural Modulus - 1% Secant | |||
| -- | 240 | MPa | ASTM D790 |
| -- | 80.0 | MPa | ASTM D2457 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested 1 | 25 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 25 µm, Blown Film | 25.0 | MPa | |
| TD : Break, 25 µm, Blown Film | 20.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 25 µm, Blown Film | 390 | % | |
| TD : Break, 25 µm, Blown Film | 900 | % | |
| Dart Drop Impact 2(Blown Film) | 90 | g | ASTM D1709 |
| Elmendorf Tear Strength - TD (Blown Film) | 55 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 86.0 | °C | ASTM D1525 3 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°, 25.0 µm, Blown Film) | 78 | ASTM D2457 | |
| Haze (25.0 µm, Blown Film) | 12 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 130 to 180 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 to 310 | °C |
| Note Message | |
|---|---|
| 1 . | 75mm extruder, die gap 1.0mm, output 1.75 kg/h*cm with 2:1 BUR. |
| 2 . | F50 |
| 3 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| STABAMID® 26 FS 1 | Solvay Polyamide & Intermediates | Nylon 66 | STABAMID® |
| CMET HS-696 | CMET Inc. | Epoxy | CMET |
| DAI-EL™ G-211 | Daikin Fluorochemicals (China) Co., Ltd. | Fluorelastomer | DAI-EL™ |
| Elastollan® 688A50N | BASF Corp. Thermoplastic Polyurethanes | TPU-Polyester | Elastollan® |
| LUVOCOM® 100-8758 | Lehmann & Voss & Co. | PUR, Unspecified | LUVOCOM® |