Tarnamid® T- 27 MT 20
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Grupa Azoty S.A. |
| Trademark: | Tarnamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | I57v4A_Tarnamid-T--27-MT-20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| It is 20% mineral reinforced polyamide 6 compound, heat stabilised. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.27 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 90.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.80 | % | |
| Flow : 2.00 mm | 0.40 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.1 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 175 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5600 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 72.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 6.0 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 4400 | MPa | ISO 178 |
| Flexural Stress 2 | 105 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 3.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 55 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | 3.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 95.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 200 | °C | ISO 306/B |
| Melting Temperature | 221 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength (2.00 mm) | 24 | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 Hz) | 3.90 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 550 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 650 | °C | IEC 60695-2-12 |
| Burning Rate | + | FMVSS 302 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ISO Type | PA6, MHR, 14-050, MD20 | ISO 1874 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Suggested Max Moisture | < 0.10 | % | |
| Suggested Max Regrind | 10 | % | |
| Processing (Melt) Temp | 240 to 260 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Pressure | 80.0 to 110 | MPa | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Multiuse Leostomer® LJ-3170N | Riken Technos Corp. | TPU, Unspecified | Multiuse Leostomer® |
| Evoprene™ Super G 949 | AlphaGary | SEBS | Evoprene™ Super G |
| DuraGrip® DGR 6850NC | Advanced Polymer Alloys | TPE | DuraGrip® |
| POTICON IT6B | Otsuka Chemical Co., Ltd. | PEI | POTICON |
| LEXAN™ EM1210 resin | SABIC Innovative Plastics | PC | LEXAN™ |