HiFill® PC / PBT GF 30 BK
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | HiFill® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | I56hq4_HiFill-PC-PBT-GF-30-BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HiFill® PC / PBT GF 30 BK is a Polycarbonate + PBT (PC+PBT) product filled with 30% glass fiber. It can be processed by injection molding and is available in North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.50 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.060 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 119 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 107 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 6210 | MPa | ASTM D790 |
| Flexural Strength | 183 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 210 | °C | |
| 1.8 MPa, Unannealed | 173 | °C | |
| CLTE - Flow | 2.3E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 98.9 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 238 to 266 | °C | |
| Middle Temperature | 238 to 266 | °C | |
| Front Temperature | 238 to 266 | °C | |
| Processing (Melt) Temp | 238 to 266 | °C | |
| Mold Temperature | 54.4 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.414 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vexel 5100 RD | Custom Resins Group | PBT | Vexel |
| Nipol® NBR DN101L | Zeon Corporation | NBR | Nipol® NBR |
| KumhoSunny ABS HAG5223 | Shanghai KumhoSunny Plastics Co., Ltd. | ABS | KumhoSunny ABS |
| LG PMMA ID178 | LG MMA Corp. | Acrylic (PMMA) | LG PMMA |
| Kinta FR2600 | Kinta Technology (Hong Kong) Co., Ltd. | PP, Unspecified | Kinta |