MARCOBLEND AU 7100 GY01
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | POLY GIN |
| Trademark: | MARCOBLEND |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | I3WN7u_MARCOBLEND-AU-7100-GY01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| MARCOBLEND AU 7100 GY01 is a mid light reflective rate and ignition resistant polycarbonate/ABS/GF 10% resin. The resin is Halogen free and compliance with TCO and RoHS certification. The unique characters include superior processability, high light reflective and suitable for use in notebook, LCD TV/ Monitor back light frame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (240°C/5.0 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.20 to 0.40 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 59.7 | MPa | ASTM D638 |
| Flexural Modulus | 2890 | MPa | ASTM D790 |
| Flexural Strength | 105 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 119 | °C | ASTM D648 |
| CLTE | ASTM D696 | ||
| Flow | 4.5E-5 | cm/cm/°C | |
| Transverse | 6.5E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 250 to 270 | °C | |
| Middle Temperature | 250 to 270 | °C | |
| Front Temperature | 260 to 280 | °C | |
| Nozzle Temperature | 260 to 280 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resinoid 2002-2 | Resinoid Engineering Corporation | Phenolic | Resinoid |
| Lotader® 8200 | Arkema | EEA | Lotader® |
| LUVOCOM® 1105-8344/EM/GY | Lehmann & Voss & Co. | PEEK | LUVOCOM® |
| Paracril® P7083P | INSA | NBR | Paracril® |
| TECHLEN SD810 | DAEHA Co., LTD | PP, Unspecified | TECHLEN |