LNP™ THERMOCOMP™ WF006 compound
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | I3KbUg_LNPTHERMOCOMPWF006compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP THERMOCOMP WF006 is a compound based on Polybutylene Terephalate resin containing Glass Fiber. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.53 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.28 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 140 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.5 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 8000 | MPa | ISO 178 |
| Flexural Stress | 191 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 2(23°C) | 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 50 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4 | |||
| 0.45 MPa, unannealed, 64.0mm span | 222 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64.0mm span | 203 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 3.2E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 221 - 232 | °C | |
| Middle Temperature | 243 - 254 | °C | |
| Front Temperature | 260 - 271 | °C | |
| Processing (Melt) Temp | 238 - 266 | °C | |
| Mold Temperature | 82.2 - 98.9 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| APEX® 83-F279-A | Teknor Apex Company | PVC, Flexible | APEX® |
| Daicel PP PNAH5 | Daicel Polymer Ltd. | PP, Unspecified | Daicel PP |
| Formolene® 3435E | Formosa Plastics Corporation, U.S.A. | PP Random Copolymer | Formolene® |
| K-Prene 7000 XL 65 | Technovinyl Polymers India Ltd. | TPV | K-Prene |
| Lion Idemitsu Composites PPS G141Z1 | Lion Idemitsu Composites Co., Ltd. | PPS | Lion Idemitsu Composites PPS |