LONGLITE® LCP LCP-300 N3G
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | CCP Group |
| Trademark: | LONGLITE® LCP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | I28nya_LONGLITE-LCP-LCP-300-N3G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LCP-300/ LCP-270 is a high heat-resistance and anisotropic, Type I/ Type II grade Liquid Crystalline Polymer Compound LCP-300/LCP-270 appears low viscosity and high fluidity while operating temperature is higher than its melting point. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.61 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 160 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 15500 | MPa | ISO 178 |
| Flexural Stress (23°C) | 225 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 22 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 295 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (2.00 mm) | > 13 | kV/mm | ASTM D149 |
| Arc Resistance | 150 | sec | ASTM D495 |
| Comparative Tracking Index | 175 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 140 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 330 to 350 | °C | |
| Middle Temperature | 350 to 370 | °C | |
| Front Temperature | 360 to 390 | °C | |
| Nozzle Temperature | 360 to 390 | °C | |
| Mold Temperature | 40.0 to 120 | °C | |
| Injection Pressure | 98.1 to 137 | MPa | |
| Holding Pressure | 29.4 to 68.6 | MPa | |
| Back Pressure | 0.800 to 1.00 | MPa | |
| Screw Speed | 40 to 120 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PP 83MF10 | Saudi Basic Industries Corporation (SABIC) | PP Impact Copolymer | SABIC® PP |
| Thermec™ 4140RMC50 | Technical Polymers, LLC | PPS | Thermec™ |
| Xuchuan XCS-2033B | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| FHR Polypropylene P5C4Z-090 | Flint Hills Resources, LP | PP Random Copolymer | FHR Polypropylene |
| PermaStat® 105 | RTP Company | PP, Unspecified | PermaStat® |