MEGOLON™ HF 8110 LD NATURAL UV
| Category: | TP, Unspecified , Thermoplastic |
| Manufacturer: | AlphaGary |
| Trademark: | MEGOLON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | I1w1BS_MEGOLON-HF-8110-LD-NATURAL-UV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A THERMOPLASTIC, ZERO-HALOGEN, UV RESISTANT, FLAME RETARDED, 60°C RATED, OLEFINIC JACKETING COMPOUND INTENDED FOR TELECOMMUNICATIONS CABLE (IEC 332-1). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.50 - 1.54 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/10.0 kg) | 10 - 16 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw D | 59 - 65 | ASTM D2240 | |
| Shaw D, 15 seconds | 49 - 55 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (0.762 mm) | 11.0 | MPa | ASTM D412 |
| Tensile Elongation (Break, 0.762 mm) | 150 | % | ASTM D412 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air 1(100°C, 168 hr) | 10 | % | UL Unspecified |
| Change in Ultimate Elongation in Air 2(100°C, 168 hr) | -25 | % | UL Unspecified |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -15.0 | °C | ASTM D746 |
| Hot pressing test- % Loss (80°C) | 35 | % | IEC 811-3-1 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Extruder Screw Compression Ratio | 1.5:1.0 to 2.5:1.0 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Constant (23°C, 100 MHz) | 3.50 | ASTM D150 | |
| Dissipation Factor (23°C, 100 MHz) | 0.013 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index (3.18 mm) | 34 | % | ASTM D2863 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Cylinder Zone 1 Temp. | 154 | °C | |
| Cylinder Zone 2 Temp. | 160 | °C | |
| Cylinder Zone 3 Temp. | 166 | °C | |
| Cylinder Zone 4 Temp. | 171 | °C | |
| Cylinder Zone 5 Temp. | 171 | °C | |
| Adapter Temperature | 177 | °C | |
| Melt Temperature | 171 - 182 | °C | |
| Die Temperature | 177 | °C |
| Extrusion instructions |
|---|
| Barrier ScrewScreen Pack: 20/20 or 20/40 |
| Note Message | |
|---|---|
| 1 . | Thickness: 30 mil |
| 2 . | Thickness: 30 mil |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren Q281 (1st-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | LDPE | Sanren |
| Styropor® P 656 | BASF Corporation | PS (EPS) | Styropor® |
| Kazan LDPE 15313-003 OKP 22 1111 2003 | Kazanorgsintez Joint Stock Company | LDPE | Kazan LDPE |
| TechnoElast A 7000 I 1 nat | TechnoCompound GmbH | TPE | TechnoElast |
| Sylvin 2990-82 Clear 8463 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |