Pinnacle PP 6180C3
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | Pinnacle Polymers |
| Trademark: | Pinnacle PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | I1olGF_Pinnacle-PP-6180C3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
80 MELT FLOW CLARIFIED RANDOM COPOLYMER FOR INJECTION MOLDING Pinnacle Polymers Polypropylene 6180C3 is made via UNIPOL™ PP technology, which utilizes gas-phase fluidized bed reactors with a high activity catalyst system to ensure uniform physical properties and lot-to-lot consistency. This product is intended for injection molding applications that require high melt flow, more stiffness, faster cycle time, low bloom, enhanced processability and excellent clarity. This product contains a new generation clarifier. The 6180C3 product provides:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 80 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.5 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm, Injection Molded) | 28.3 | MPa | ASTM D638 |
| Tensile Elongation 2(Yield, 3.20 mm, Injection Molded) | 14 | % | ASTM D638 |
| Flexural Modulus - 1% Secant 3(3.20 mm, Injection Molded) | 1100 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 4(23°C, 3.20 mm, Injection Molded) | 48 | J/m | ASTM D256 |
| Notched Izod Impact (Area) 5(23°C, 3.20 mm, Injection Molded) | 4.70 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 78.0 | °C | ASTM D648 |
| Optical | Nominal Value | Unit | |
|---|---|---|---|
| Haze (1270 µm) | 9.0 | % | |
| Yellowness Index | < -10 | YI |
| Note Message | |
|---|---|
| 1 . | Type I, 51 mm/min |
| 2 . | Type I, 51 mm/min |
| 3 . | Type I, 1.3 mm/min |
| 4 . | Type I |
| 5 . | Type I |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 6 MKF 3010 H | A. Schulman Europe | Nylon 6 | SCHULAMID® |
| Skyrol® SH92 | SKC Inc. | PET | Skyrol® |
| SUMILITE® PL-1186 | Sumitomo Bakelite Co., Ltd. | Phenolic | SUMILITE® |
| Toler EVA 182 | Toler Chemical, Inc | EVA | Toler EVA |
| XANTAR® 22 R | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |