LNP™ STAT-KON™ MD000 compound
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | I1I4uL_LNPSTATKONMD000compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON* MD000 is a compound based on Polypropylene resin containing Carbon Powder. Added features of this material include: Electrically Conductive. Also known as: LNP* STAT-KON* Compound M Product reorder name: MD000 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.950 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 1.3 - 1.6 | % | ASTM D955 |
| Transverse flow : 24 hours | 1.3 - 1.6 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 1.3 | % | ISO 294-4 |
| Flow direction : 24 hours | 1.5 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.030 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.030 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1250 | MPa | ASTM D638 |
| -- | 1220 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 21.9 | MPa | ASTM D638 |
| Yield | 21.5 | MPa | ISO 527-2 |
| Fracture | 16.9 | MPa | ASTM D638 |
| Fracture | 16.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 8.4 | % | ASTM D638 |
| Yield | 6.3 | % | ISO 527-2 |
| Fracture | 48 | % | ASTM D638 |
| Fracture | 52 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 1180 | MPa | ASTM D790 |
| -- | 1160 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 29.2 | MPa | ASTM D790 |
| -- | 24.9 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 820 | J/m | ASTM D256 |
| 23°C 2 | 60 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | No Break | ASTM D4812, ISO 180/1U | |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 33.4 | J | ASTM D3763 |
| -- | 32.8 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 51.7 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 3 | 53.0 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 1.0E-4 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 1.0E-4 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 - 1.0E+6 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 193 - 204 | °C | |
| Middle Temperature | 216 - 227 | °C | |
| Front Temperature | 238 - 249 | °C | |
| Processing (Melt) Temp | 227 - 249 | °C | |
| Mold Temperature | 32.2 - 48.9 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® COPP 35.2.0 | Marco Polo International, Inc. | PP Copolymer | MARPOL® COPP |
| RTP 2700 S-50A | RTP Company | SEBS | RTP |
| NEFTEKHIM PE 4152L (524F6) | Nizhnekamskneftekhim Inc. | HDPE | NEFTEKHIM PE |
| Chansieh Phenolic J-661 | Chansieh Enterprises Co., LTD. | Phenolic | Chansieh Phenolic |
| Rotec® ABS 1002 FR V0/5 | ROMIRA GmbH | ABS | Rotec® ABS |