LNP™ LUBRICOMP™ BX03658N compound
| Category: | SAN , Styrene Acrylonitrile |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | I0pzGW_LNP-LUBRICOMP-BX03658N-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP BX03658N is a compound based on SAN resin containing proprietary fillers. Added features of this grade include: Wear Resistant, Tight Dimensional Tolerances, good for Water Meter Applications. Also known as: LNP* LUBRICOMP* Compound BX03658N Product reorder name: BX03658N |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.30 to 0.50 | % | |
| Across Flow : 24 hr | 0.40 to 0.60 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.11 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.16 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 6520 | MPa | ASTM D638 |
| -- | 6140 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 52.0 | MPa | ASTM D638 |
| Break | 50.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 1.5 | % | ASTM D638 |
| Break | 1.5 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 6320 | MPa | ASTM D790 |
| -- 5 | 6070 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 80.1 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 84.0 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.36 | ||
| vs. Itself - Static | 0.44 | ||
| Wear Factor | ASTM D3702 Modified | ||
| Ring | 11.0 | 10^-10 in^5-min/ft-lb-hr | |
| Washer | 163 | 10^-10 in^5-min/ft-lb-hr |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 17 | J/m | ASTM D256 |
| 23°C 7 | 2.3 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 120 | J/m | ASTM D4812 |
| 23°C 8 | 8.4 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 2.70 | J | ASTM D3763 |
| -- | 0.840 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 101 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 101 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 95.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 96.0 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 4.6E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 5.3E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 204 to 216 | °C | |
| Middle Temperature | 243 to 254 | °C | |
| Front Temperature | 277 to 288 | °C | |
| Processing (Melt) Temp | 260 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PrimaFlex® HP 1200 | Plastic Solutions, Inc. | PP Homopolymer | PrimaFlex® |
| DENYL HT 2010 Y | Vamp Tech | PPA+Nylon | DENYL |
| Elastollan® 1195A10R | BASF Corp. Thermoplastic Polyurethanes | TPU-Polyether | Elastollan® |
| LCA® PC-120 Black | UniPlas, Inc. | PC | LCA® |
| PLUSTEK PB304G7 | Polyram Ram-On Industries | Nylon 6 | PLUSTEK |