Asrene® SM 5508
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Chandra Asri Petrochemical |
| Trademark: | Asrene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HzpGBf_Asrene-SM-5508.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Asrene®SM 5508 is a high density polyethylene product,. It can be processed by film extrusion, co-extrusion or filament extrusion, and is available in North America, Europe or Asia Pacific. Asrene®SM 5508 applications include movies, slings/ropes, textiles/fibers, glue/gummed paper and yarns. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.954 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.75 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (F50) | 155 | hr | ASTM D1693 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 20 | µm | |
| Elastic Modulus - MD (20 µm, Blown Film) | 600 | MPa | ASTM D882 |
| Elastic Modulus - TD (20 µm, Blown Film) | 750 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Broken, 20 µm, blown film | 70.0 | MPa | ASTM D882 |
| TD : Broken, 20 µm, blown film | 60.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 20 µm, blown film | 650 | % | ASTM D882 |
| TD : Broken, 20 µm, blown film | 750 | % | ASTM D882 |
| Dart Drop Impact (20 µm, Blown Film) | 50 | g | ASTM D1709 |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 20.0 µm | 11.8 | kN/m | ASTM D1922 |
| TD : 20.0 µm | 58.8 | kN/m | ASTM D1922 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Impact Strength - Blown Film (20.0 µm) | 15.7 | J/cm | ASTM D3420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 129 | °C | ASTM D1525 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 - 220 | °C |
| Extrusion instructions |
|---|
| Blow-up Ratio: 3 to 5 |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYFORT® FPP 30 GFC | A. Schulman Europe | PP Homopolymer | POLYFORT® |
| RTP 881 TFE 10 DEL | RTP Company | Acetal (POM) Copolymer | RTP |
| UBE Nylon 1013IU50 | UBE Industries, Ltd. | Nylon 6 | UBE Nylon |
| LUCITE® 41 | Lucite International Inc. | Acrylic (PMMA) | LUCITE® |
| Kinta AG15A1 | Kinta Technology (Hong Kong) Co., Ltd. | ABS | Kinta |