STYRON™ 636 BT

Category:	PS (GPPS) , General Purpose Polystyrene Resin
Manufacturer:	Trinseo
Trademark:	STYRON™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	Hzexyh_STYRON636BT.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

STYRON™ 636 BT is a general purpose polystyrene with a specific Blue Tone color designed for injection molded appliance applications. It is a high molecular weight material suitable for extrusion blending with high impact polystyrene. Its high strength makes it ideally suited for packaging applications and refrigerator accessories.

Applications:

Injection molded appliance accessories and containers with a light blue tint

Packaging foam extrusion

Thermoformed containers blended with HIPS

Complies with:

Europe REGULATION (EC)10/2011

U.S. FDA 21 CFR 177.1640

Consult the regulations for complete details.

General Information
Features	High molecular weight High strength
Uses	Packaging Electrical appliances Mixing Home appliance components Container
Agency Ratings	FDA 21 CFR 177.1640 Europe No 10/2011
Appearance	Blue
Forms	Particle
Processing Method	Foam extrusion molding Sheet extrusion molding Thermoforming Injection molding

Physical	Nominal Value	Unit	Test Method
Density
--	1.05	g/cm³	ISO 1183
--	1050	kg/m³	ISO 1183 ¹
Apparent Density	0.60	g/cm³	ISO 60
Melt Mass-Flow Rate (MFR) (200°C/5.0 kg)	3.1	g/10 min	ISO 1133
Water Absorption (Saturation)	0.0	%	ISO 62 ²
Viscosity Number	116	cm³/g	ISO 307, 1157, 1628 ³

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (R-Scale)	105		ISO 2039-2
Ball Indentation Hardness	150	MPa	ISO 2039-1

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	3300	MPa	ISO 527-2 ⁴
Tensile Stress
Yield	55.0	MPa	ISO 527-2/5
Yield	48.0	MPa	ISO 527-2 ⁵
Tensile Strain
Yield	2.0	%	ISO 527-2 ⁶
Fracture	2.0	%	ISO 527-2/5
Tensile Elongation at Break	3.0	%	ISO 527-2 ⁷
Flexural Modulus	3500	MPa	ISO 178
Flexural Stress	80.0	MPa	ISO 178

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, annealed	92.8	°C	ISO 75-2/B
1.8 MPa, annealed	90.0	°C	ISO 75-2/A
Vicat Softening Temperature	96.5	°C	ISO 306/A120
Linear expansion coefficient			ISO 11359-2 ⁸
Flow	8.0E-5	cm/cm/°C	ISO 11359-2
Lateral	7.0E-5	cm/cm/°C	ISO 11359-2

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	1.0E+13	ohms	IEC 60093 ⁹
Volume Resistivity	> 1.0E+15	ohms·m	IEC 60093 ¹⁰
Electric strength	140	kV/mm	IEC 60243-1 ¹¹
Dielectric Constant
1 MHz	2.50		ASTM D150, IEC 60250 ¹²
100 Hz	2.50		IEC 60250 ¹³
Dissipation Factor
1 MHz	6.0E-5		ASTM D150, IEC 60250 ¹⁴
100 Hz	9.0E-5		IEC 60250 ¹⁵

Flammability	Nominal Value	Unit	Test Method
Flame Rating ¹⁶(1.6 mm)	HB		UL 94
Burning Behav. at 1.6mm nom. thickn. (1.60 mm, UL)	HB		ISO 1210 ¹⁷

Note Message
1 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
2 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
3 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
4 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
5 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
6 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
7 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
8 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
9 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
10 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
11 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
12 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
13 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
14 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
15 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
16 .	This rating is not intended to reflect the danger caused by this or any other material under actual fire conditions.
17 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???

Resin Grade	Manufacturer	Category	Trademark
Zhongfa PA66 DD2	Yuyao Zhongfa Engineering Plastics Co. Ltd.	Nylon 6	Zhongfa
Hifax TKC 5480X	LyondellBasell Industries	PP Copolymer	Hifax
LEXAN™ FXD1413T resin	SABIC Innovative Plastics	PC	LEXAN™
Lucky Enpla LMF3250	Lucky Enpla Co LTD	PBT	Lucky Enpla
EPALINE 392A55	Epaflex Polyurethanes S.R.L.	TPU-Polyester	EPALINE