Polylink Polymer PP 411-401 (CL)
| Category: | XLPE , Crosslinked Polyethylene |
| Manufacturer: | Polylink Polymers (India) Ltd. |
| Trademark: | Polylink Polymer |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HzP6dO_Polylink-Polymer-PP-411-401-CL-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
A Silane Grafted Crosslinkable Polyethylene Compound, Curable by exposure to moisture, for insulation of Power Cables and possessing excellent extrudability at output rate. PP 411 has been specially developed for cables upto 11KV. The special formulation and compounding techniques used ensure that the contamination level is kept within the required limits for this voltage grade. PP 411 has general Melt Flow Index range of 0.5-0.8, which provides firm stability during extrusion, especially for the thick insulation required for high voltage. Silane Grafted Crosslinkable Polyethylene For Medium Voltage Power Cable Insulation. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.925 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.55 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 18.0 | MPa | IEC 60811 |
| Tensile Strain (Break) | 650 | % | IEC 60811 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (135°C, 168 hr) | 6.0 | % | IEC 60811 |
| Change in Tensile Strain at Break in Air (135°C, 168 hr) | -6.0 | % | IEC 60811 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset | IEC 60811 | ||
| Elongation underload | 110 | % | IEC 60811 |
| Permanent elongation after cooling | 5.0 | % | IEC 60811 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Power factor (23°C) 1 | 4.00E-4 | IEC 250 | |
| Volume Resistivity (20°C) | 1.4E+16 | ohms·cm | IEC 60502 |
| Dielectric Strength | 25 | kV/mm | IEC 60243-1 |
| Dielectric Constant | 2.20 | IEC 60250 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 160 | °C | |
| Cylinder Zone 2 Temp. | 170 | °C | |
| Cylinder Zone 3 Temp. | 180 | °C | |
| Cylinder Zone 4 Temp. | 190 | °C | |
| Adapter Temperature | 200 | °C | |
| Die Temperature | 210 | °C |
| Extrusion instructions |
|---|
| Screw water temperature : 60 to70°CScreens : 30,80, 30(mesh apertures per linear inch)L/D Ratio: 20Compression: 3.0:1 |
| Note Message | |
|---|---|
| 1 . | 50 Hz |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Zhongfa PP FR-18 | Yuyao Zhongfa Engineering Plastics Co. Ltd. | PP, Unspecified | Zhongfa |
| Network Polymers HDPE 50 0149 | Network Polymers, Inc. | EHMWPE | Network Polymers HDPE |
| Ferro PP TPP20AJ40UL WHITE | Ferro Corporation | PP Homopolymer | Ferro PP |
| KOPLA PA6 KNE1030 | KOPLA Co., Ltd. | Nylon 6 | KOPLA PA6 |
| Lucky Enpla LAY8008L | Lucky Enpla Co LTD | ASA+PC | Lucky Enpla |