CABELEC® CA3896
| Category: | PS (GPPS) , General Purpose Polystyrene |
| Manufacturer: | Cabot Corporation |
| Trademark: | CABELEC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HzGYz4_CABELECCA3896.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CABELEC CA3896 is an electrically conductive compound based on conductive carbon black dispersed in a modified styrenic resin. The electrical properties are permanent and are not dependent on atmospheric conditions. Applications CABELEC CA3896 has been specially designed for packaging and electronic product handling where freedom from the hazard of electrostatic discharge is necessary. Examples of use are in handling of explosives, electronic components and pigments. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.09 | g/cm³ | Internal method |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 200°C/10.0 kg | 5.0 | g/10 min | ISO 1133 |
| 200°C/21.6 kg | 38 | g/10 min | ISO 1133 |
| 200°C/5.0 kg | 1.0 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 75 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 30.4 | MPa | ISO 527-2 |
| Fracture | 24.3 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 23 | % | ISO 527-2 |
| Flexural Modulus | 1880 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 16 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 72.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 101 | °C | ISO 306/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity (0.400 mm) | 2.1E+3 | ohms | Internal method |
| Volume Resistivity | 3.0E+2 | ohms·cm | Internal method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.0 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 200 | °C | |
| Middle Temperature | 200 | °C | |
| Front Temperature | 200 | °C | |
| Nozzle Temperature | 235 | °C | |
| Mold Temperature | 30 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Cylinder Zone 1 Temp. | 170 - 200 | °C | |
| Cylinder Zone 3 Temp. | 170 - 200 | °C | |
| Cylinder Zone 5 Temp. | 170 - 200 | °C | |
| Melt Temperature | < 230 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MIRASON™ 11P | Mitsui Chemicals, Inc. | LDPE | MIRASON™ |
| Sinvicomp SRF3705E | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| Starglas CF006 | Eurostar Engineering Plastics | TES | Starglas |
| THERMOLAST® K TF9AAA (Series: FC/HE/tl) | KRAIBURG TPE | TPE | THERMOLAST® K |
| POLIMAXX 1111NXGA6 | IRPC Public Company Limited | PP Homopolymer | POLIMAXX |