MEGOLON™ S552

Category:	TP, Unspecified , Thermoplastic
Manufacturer:	AlphaGary
Trademark:	MEGOLON™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	HysWK9_MEGOLON-S552.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

MEGOLON™ S552 is a thermoplastic, halogen free, fire retardant cable sheathing compound with enhanced resistance to degradation by hot water, formulated specifically to meet the requirements of UK specification BS 7655 : 6.1 type LTS4.

APPLICATIONS

UK: BS7655 : 6.1 type LTS4. Also meets the requirements of BS7655 : 6.1 types LTS1, LTS2, LTS3 and BS7655 : 4.1 type TM1 for a general purpose PVC sheathing compound

Germany: DIN VDE 0207, part 24, type HM4. Also meets the requirements of DIN VDE 0207, part 24, type HM2

General Information
Features	Flame Retardant Halogen Free
Uses	Cable Jacketing
Agency Ratings	BS 7655 4.1 Type TM1 BS 7655:6.1 Type LTS 1 BS 7655:6.1 Type LTS 2 BS 7655:6.1 Type LTS 3 BS 7655:6.1 Type LTS 4 DIN VDE 0207 Part 24, Type HM4 DIN VDE 0207, Part 24, Type HM2
Forms	Pellets
Processing Method	Extrusion

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.51	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (150°C/21.6 kg)	5.5	g/10 min	ISO 1133

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D)	59		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress
-- ¹	15.0	MPa	IEC 60811-1-2
-- ²	17.0	MPa	IEC 60811-1-2
--	14.0	MPa	IEC 60811-1-1
Tensile Strain
Break ³	170	%	IEC 60811-1-2
Break	200	%	IEC 60811-1-1
Elongation at Break
after 4 hours, in IRM 902 Oil : 70°C	210	%
after 4 hours, in SAE 20 Oil : 70°C	180	%
after 7 days, in IRM 902 Oil : 23°C	220	%
after 7 days, in IRM 903 Oil : 23°C	160	%
Tensile Strength
after 4 hours, in IRM 902 Oil : 70°C	13.5	MPa
after 4 hours, in SAE 20 Oil : 70°C	13.5	MPa
after 7 days, in IRM 902 Oil : 23°C	14.5	MPa
after 7 days, in IRM 903 Oil : 23°C	12.5	MPa

Thermal	Nominal Value	Unit	Test Method
Hot Pressure Test (90°C)	35	%	IEC 60811-3-1

Electrical	Nominal Value	Unit	Test Method
Insulation Resistance - after 12 hours immersion in water (20°C)	1.0E+14	ohms·cm	BS 6469 99.2

Flammability	Nominal Value	Unit	Test Method
Acid Gas Emission Conductivity	4.00	µS/cm	IEC 60754-2
Acid Gas Emission pH	5.70		IEC 60754-2
Flammability Temperature Index	280	°C	ISO 4589-3
Smoke Density ⁴			ASTM E662
Flaming mode	< 60	Ds
Non-flaming mode	< 140	Ds
Toxicity	0.600		NES 713

Additional Information	Nominal Value	Unit	Test Method
Halogen Acid Gas Evolution	0.0	%	IEC 60754-1

Extrusion	Nominal Value	Unit
Draw Down	1.5:1.0
Extruder Screw Compression Ratio	1.0:1.0 to 2.0:1.0

Elastomers	Nominal Value	Unit	Test Method
Tear Strength	8.00	kN/m	BS 6469 99.1

Aging	Nominal Value	Unit	Test Method
Change in Tensile Strength in Air
100°C, 168 hr	5.0	%
110°C, 168 hr	20	%
Change in Tensile Strain at Break in Air
100°C, 168 hr	-15	%
110°C, 168 hr	-15	%
Change in Tensile Stress
23°C, 168 hr, in IRM 902 Oil	5.0	%
23°C, 168 hr, in IRM 903 Oil	-10	%
70°C, 4 hr, in IRM 902 Oil	-5.0	%
70°C, 4 hr, in SAE 20 Oil	-5.0	%
70°C, 168 hr, in Water	-12	%	BS 6469 99.1
Change in Tensile Strain at Break
23°C, 168 hr, in IRM 902 Oil	10	%
23°C, 168 hr, in IRM 903 Oil	-20	%
70°C, 4 hr, in IRM 902 Oil	5.0	%
70°C, 4 hr, in SAE 20 Oil	-10	%
70°C, 168 hr, in Water	-5.0	%	BS 6469 99.1

Flammability	Nominal Value	Unit	Test Method
Oxygen Index	36	%	ISO 4589-2

Extrusion	Nominal Value	Unit
Drying Temperature	60.0 to 70.0	°C
Cylinder Zone 1 Temp.	135	°C
Cylinder Zone 2 Temp.	140	°C
Cylinder Zone 3 Temp.	145	°C
Cylinder Zone 4 Temp.	150	°C
Cylinder Zone 5 Temp.	160	°C
Melt Temperature	165 to 175	°C
Die Temperature	165	°C

Note Message
1 .	after 7 days at 100°C
2 .	after 7 days at 110°C
3 .	after 7 days at 100°C
4 .	Time to maximum: 12 minutes

Resin Grade	Manufacturer	Category	Trademark
Tarnamid® T- 27 GF30 FRV2	Grupa Azoty S.A.	Nylon 6	Tarnamid®
Varcum 92600	Durez Corporation	Phenolic	Varcum
Hanwha Total PP TB70W	HANWHA TOTAL PETROCHEMICALS Co., Ltd.	PP, High Crystal	Hanwha Total PP
Hifax TRC 298P	LyondellBasell Industries	PP Impact Copolymer	Hifax
Hifax X M1 T11 BLACK	LyondellBasell Industries	PP Copolymer	Hifax