Exelene® HDPE 8000
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Montachem International, Inc. |
| Trademark: | Exelene® HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HymXx6_Exelene-HDPE-8000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Exelene HDPE 8000: Antioxidant Exelene HDPE 8000UV: Antioxidant, UV Stabilzer |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.961 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 8.5 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (50°C, 1.90 mm, 100% Igepal CO-630, F50) | 3.00 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 1 sec, 23°C) | 70 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 31.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | > 600 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 1210 | MPa | ASTM D790B |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 53 | J/m | ASTM D256A |
| Tensile Impact Strength | 168 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 87.0 | °C | ASTM D648 |
| Brittleness Temperature 4 | < -75.0 | °C | ASTM D746A |
| Vicat Softening Temperature | 128 | °C | ASTM D1525 5 |
| Melting Temperature | 133 | °C | DSC |
| Note Message | |
|---|---|
| 1 . | Type IV, 50 mm/min |
| 2 . | Type IV, 50 mm/min |
| 3 . | Type I, 13 mm/min |
| 4 . | F50; 25 lbf-in |
| 5 . | Rate A (50°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SuperLite® SL552000-100 (8.0mm) | Azdel, Inc. | PP, Unspecified | SuperLite® |
| Keyflex® BT 1045D | LG Chem Ltd. | TPC-ET | Keyflex® BT |
| KRATON® A1535 H | Kraton Polymers LLC | SEBS | KRATON® |
| Hostacom HKC 431N C12334 | LyondellBasell Industries | PP Homopolymer | Hostacom |
| Polyrocks EP8400X125F-1 | Polyrocks Chemical Co., Ltd | XLPE | Polyrocks |