ULTEM™ LTX300B resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HylBfC_ULTEM-LTX300B-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Standard flow Polyetherimide blend with low toxicity, smoke, and flame evolution. ECO Compliant, UL94 V0 listing. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (295°C/6.6 kg) | 1.6 | g/10 min | ASTM D1238 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.30 to 0.50 | % | |
| Across Flow : 3.20 mm | 0.50 to 0.70 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 3340 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 96.5 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 88 | % | ASTM D638 |
| Flexural Modulus 4(100 mm Span) | 3210 | MPa | ASTM D790 |
| Flexural Strength 5 | ASTM D790 | ||
| Yield, 100 mm Span | 145 | MPa | |
| Break, 100 mm Span | 141 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 80 | J/m | ASTM D256 |
| Reverse Notch Izod Impact (3.20 mm) | 2100 | J/m | ASTM D256 |
| Gardner Impact (23°C) | 35.3 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 191 | °C | ASTM D648 |
| RTI Elec | 140 | °C | UL 746 |
| RTI Imp | 115 | °C | UL 746 |
| RTI Str | 140 | °C | UL 746 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Arc Resistance 6 | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 4 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 3 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 0 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.762 mm) | V-0 | UL 94 | |
| Halogen Content | 0 | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 135 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Drying Time, Maximum | 12 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 310 to 332 | °C | |
| Middle Temperature | 321 to 343 | °C | |
| Front Temperature | 332 to 354 | °C | |
| Nozzle Temperature | 327 to 349 | °C | |
| Processing (Melt) Temp | 332 to 354 | °C | |
| Mold Temperature | 93.3 to 135 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 2.6 mm/min |
| 5 . | 2.6 mm/min |
| 6 . | Tungsten Electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU P22M | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| Sylvin 9451-90 Natural | Sylvin Technologies Incorporated | PVC+PUR | Sylvin |
| NORYL™ PX1390 resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |
| Fainplast PVC RE 330 | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| Hanwha Total PP FH22 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |