Zytel® ST801AHS BK010
| Category: | Nylon 66 , NYLON RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HyhkaM_ZytelST801AHSBK010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Super Toughened, Heat Stabilized, Polyamide 66 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.09 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Transverse flow | 1.4 | -- | % | ISO 294-4 |
| Flow | 1.8 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 1.1 | -- | % | ISO 62 |
| Balance, 23°C, 2.00mm, 50% RH | 2.0 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 107 | 69 | ISO 2039-2 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2000 | 1100 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 47.0 | 39.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 4.0 | 39 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 50 | > 50 | % | ISO 527-2 |
| Flexural Modulus | 1900 | 800 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 17 | 15 | kJ/m² | ISO 179/1eA |
| 23°C | 75 | 110 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | -- | ISO 179/1eU | |
| Notched Izod Impact | ISO 180/1A | |||
| -40°C | 17 | -- | kJ/m² | ISO 180/1A |
| -30°C | 19 | -- | kJ/m² | ISO 180/1A |
| 23°C | 70 | -- | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | No Break | -- | ISO 180/1U |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 147 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 61.0 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 262 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow | 1.4E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral | 1.2E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 2(1.00 mm) | 24 | -- | mm/min | ISO 3795 |
| Flame Rating | UL 94, IEC 60695-11-10, -20 | |||
| 0.75 mm | HB | -- | UL 94, IEC 60695-11-10, -20 | |
| 1.5 mm | HB | -- | UL 94, IEC 60695-11-10, -20 | |
| FMVSS Flammability | B | -- | FMVSS 302 | |
| Atomization- G-value (condensate) | 1.0E-4 | -- | g | ISO 6452 |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Emission of Organic Compounds | 13.0 | -- | µgC/g | VDA 277 |
| Odor | 5.00 | -- | VDA 270 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Melt Temperature, Optimum | 290 | °C | |
| Mold Temperature, Optimum | 80 | °C | |
| Drying Recommended | yes | ||
| Hold Pressure Time | 4.00 | s/mm | |
| Maximum Screw Tangential Speed | 300 | mm/sec |
| Fill Analysis | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ejection Temperature | 190 | -- | °C |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time - Desiccant Dryer | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 280 - 300 | °C | |
| Mold Temperature | 50 - 100 | °C | |
| Holding Pressure | 50.0 - 100 | MPa |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | FMVSS 302 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resinoid 1310 | Resinoid Engineering Corporation | Phenolic | Resinoid |
| Vydyne® 75HF | Ascend Performance Materials Operations LLC | Nylon 66/6 | Vydyne® |
| TYNELOY® NAV260 | Tyne Plastics LLC. | PPE+PS | TYNELOY® |
| Epoxies, Ect. 50-3150 FR | Epoxies, Etc. | Epoxy | Epoxies, Ect. |
| Plasmer 5035N/1002 | HYUNDAI EP Co., Ltd. | TPE | Plasmer |