K-Resin® SBC DK11
| Category: | SBC , Styrene Butadiene Block Copolymer |
| Manufacturer: | Chevron Phillips Chemical Company LLC |
| Trademark: | K-Resin® SBC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Hy2Sgf_K-Resin-SBC-DK11.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
K-Resin®SBC DK11 is a styrene-butadiene copolymer (SBC) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is: blown film or cast film. K-Resin®The main features of SBC DK11 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.01 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 7.5 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 25 µm, blown film | 1410 | MPa | ASTM D882 |
| 1% secant, TD : 25 µm, blown film | 965 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 25 µm, blown film | 34.5 | MPa | ASTM D882 |
| TD : Yield, 25 µm, blown film | 21.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 110 | % | ASTM D882 |
| TD : Broken, 25 µm, blown film | 200 | % | ASTM D882 |
| Dart Drop Impact 1(25 µm, Blown Film) | 590 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm, blown film | 7.0 | g | ASTM D1922 |
| TD : 25 µm, blown film | 15 | g | ASTM D1922 |
| Oxygen Permeability (25 µm, Blown Film) | 170 | cm³·mm/m²/atm/24 hr | ASTM D3985 |
| Water Vapor Transmission Rate (25 µm, Blown Film) | 2.2 | g·mm/m²/atm/24 hr | ASTM F1249 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Instrumented Dart Impact (0.0254 mm, Blown Film) | 0.904 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature 2 | 85.0 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gardner Gloss (25.4 µm, Blown Film) | 140 | ASTM D523 | |
| Haze 3(Blown Film) | 0.70 | % | ASTM D1003 |
| Additional Information |
|---|
| Typical blown film properties with 3% SKR17 slip/antiblock, I mil ( 0.025 mm) film (2.5:1 BUR) 35 mil ( 0.90 mm) die gap. |
| Note Message | |
|---|---|
| 1 . | 26 in |
| 2 . | Injection Molded |
| 3 . | Haze was measured using blown film containing only 1% SKR19 stabilizer, I mil ( 0.025 mm) film (2.5:1 BUR) 35 mil ( 0.90 mm) die gap. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUPREME PP SPEXP55 | Supreme Petrochem Ltd. | PP, Unspecified | SUPREME PP |
| Geon™ Vinyl Flexible B5500 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| EcolGreen EGP-200 | EcolBiotech Co., Ltd | PLA | EcolGreen |
| Hanwha Total PP BI492 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| LNP™ LUBRICOMP™ DFP34 compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |